X-Ray Diffraction Analysis of the Sintered Y-TZP-AI2O3 Ceramics

Nickolai Savchenko, Tatiana Sablina, Irina Sevostyanova, Artem Pshenichnyy, Svetlana Buyakova, Sergei Kulkov

Результат исследований: Материалы для журнала

Аннотация

The paper discusses the wear resistance, friction coefficient, and structure of friction surfaces of fine-grained (0.2 μm) Y-TZP-Al2O3 composite rubbed against a steel disk counterface at a pressure of 5 MPa in a range of sliding speeds from 1 to 20 m/sec. It is shown that, starting at 2 m/sec, the fricti on surface is subdivided by a crack network into separate regions within which local spalling occurs at the maximum wear rate and a sliding speed of 5 m/sec. X-ray diffraction reveals inversion (with respect to the initial state) of the peak intensities of the tetragonal phase with random crystalline grain orientation. The degree of this inversion increases with sliding speed. These results are discussed in terms of the effects exerted by the reorientation of martensite-free deformation twins in the tetragonal phase and the formation of a quasi-liquid film on the wear resistance of fine-grained Y-TZP-Al2O3.

Язык оригиналаАнглийский
Номер статьи012015
ЖурналIOP Conference Series: Materials Science and Engineering
Том140
Номер выпуска1
DOI
СостояниеОпубликовано - 8 авг 2016
СобытиеInternational Seminar on Interdisciplinary Problems in Additive Technologies - Tomsk, Российская Федерация
Продолжительность: 16 дек 201517 дек 2015

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Fingerprint Подробные сведения о темах исследования «X-Ray Diffraction Analysis of the Sintered Y-TZP-AI<sub>2</sub>O<sub>3</sub> Ceramics». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать