Ways of the dislocation substructure evolution in austenite steel under low and multicycle fatigue

A. V. Gromova, Yu F. Ivanov, S. V. Vorobyov, S. V. Konovalov, S. V. Gorbunov, V. E. Gromov

Результат исследований: Материалы для журнала

3 Цитирования (Scopus)

Аннотация

Analysis of dislocation substructures evolution in austenite steels 08H18N10T (0.1 wt.% C, 18 % Cr, 9 % Ni, 1 % Ti), 45G17Yu3 (0.45 wt. % C, 17 % Mn, 3 % Al) during low-cycle and multicycle fatigue tests before failure was performed by transmission electron microscopy methods. Quantity dependences of dislocation scalar density changes, lattice curvature-torsion amplitude upon load cycles numbers were determined. It allowed to analyze the dislocation substructure transformation chains, and to determine the steel fatigue failure sources.

Язык оригиналаАнглийский
Страницы (с-по)83-90
Число страниц8
ЖурналProcedia Engineering
Том2
Номер выпуска1
DOI
СостояниеОпубликовано - 1 апр 2010
Событие10th International Fatigue Congress, FATIGUE 2010 - Prague, Чешская Республика
Продолжительность: 6 июн 201011 июн 2010

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint Подробные сведения о темах исследования «Ways of the dislocation substructure evolution in austenite steel under low and multicycle fatigue». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать