The effect of friction stir welding tool wear on the weld quality of aluminum alloy AMg5M

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

6 Цитирования (Scopus)

Аннотация

Friction stir welding (FSW) tool wear has been studied from the standpoint of tribological layer generation and interaction of this layer with the tool's metal. It was shown that during FSW on aluminum alloy the latter adheres to the tool's working surface and then iron/aluminum reaction diffusion is initiated under the conditions of high mechanical stress and temperature. Since diffusion along the former austenite grain boundaries is much faster than volume diffusion, an intermetallic compound is formed inside the tool's metal thus causing embrittlement and pulling out the tool's metal fragments.

Язык оригиналаАнглийский
Название основной публикацииAIP Conference Proceedings
ИздательAmerican Institute of Physics Inc.
Страницы635-638
Число страниц4
Том1623
ISBN (электронное издание)9780735412606
DOI
СостояниеОпубликовано - 2014
СобытиеInternational Conference on Physical Mesomechanics of Multilevel Systems 2014 - Tomsk, Российская Федерация
Продолжительность: 3 сен 20145 сен 2014

Конференция

КонференцияInternational Conference on Physical Mesomechanics of Multilevel Systems 2014
СтранаРоссийская Федерация
ГородTomsk
Период3.9.145.9.14

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Подробные сведения о темах исследования «The effect of friction stir welding tool wear on the weld quality of aluminum alloy AMg5M». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать