The effect of crater creation on the fatigue strength and corrosion resistance of steels and titanium alloys irradiated by high-power pulsed ion beams

V. A. Shulov, N. A. Nochovnaia, G. E. Remnev

Результат исследований: Материалы для журналаСтатьярецензирование

28 Цитирования (Scopus)

Аннотация

The effect of high-power pulsed ion-beam (HPPIB) irradiation and various methods of the surface treatment on the crater creation phenomenon (cratering) was examined with the use of Auger electron spectroscopy. X-ray diffraction analysis, and scanning electron microscopy. They crater distribution density,sizes and shape, along with the microhardness and chemical composition inside and outside them were determined. It was shown that cratering on the surface of refractory alloys is due to the cathode material crosion and the nonstability in the physical and chemical state of the irradiated targets. The samples were treated with HPPIB. The irradiated samples were subjected to fatigue and corrosion tests. It was established that cratering leads to catastrophic fracture of the irradiated targets under the cycle load. For example, as a result of crater creation, the fatigue strength of VT18U alloy was decreased from 380 to 240 MPa. In this case the nucleation of fracture lies near the craters. Furthermore, the titanium alloys irradiated by HPPIB are subjected to pitting corrosion in seawater. It was shown that according to the test results, adjacent and dent-shape craters are the most dangerous defects under the cycle load.

Язык оригиналаАнглийский
Страницы (с-по)488-493
Число страниц6
ЖурналSurface and Coatings Technology
Том158-159
DOI
СостояниеОпубликовано - 29 окт 2002

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

Fingerprint Подробные сведения о темах исследования «The effect of crater creation on the fatigue strength and corrosion resistance of steels and titanium alloys irradiated by high-power pulsed ion beams». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать