The character of fracture of iron based thermal coating during fretting

Zh G. Kovalevskaya, E. A. Kovalevskiy, M. A. Khimich

Результат исследований: Материалы для журналарецензирование

1 Цитирования (Scopus)


The character of destruction of thermal coatings during fretting has been investigated. An iron based plasma coating has been tested with oscillation amplitude from 30 to 200 microns. The tests were conducted in air. It has been determined that the main factor influencing the rate of the wear of the coating during fretting corrosion is the size of the coating area involved into the wear process. The coating exhibits high wear resistance when the amplitude of the oscillation is commensurate with the size of the sprayed particles. During destruction of the coating the leading role belongs to fatigue-oxidation processes. The wear of the coating acquires a catastrophic character when coating macro defects - pores and interlayer boundaries - are involved into the wear process.

Язык оригиналаАнглийский
Номер статьи012126
ЖурналIOP Conference Series: Materials Science and Engineering
Номер выпуска1
СостояниеОпубликовано - 2 июн 2016
СобытиеInternational Conference on Mechanical Engineering, Automation and Control Systems 2015, MEACS 2015 - Tomsk, Российская Федерация
Продолжительность: 1 дек 20154 дек 2015

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Fingerprint Подробные сведения о темах исследования «The character of fracture of iron based thermal coating during fretting». Вместе они формируют уникальный семантический отпечаток (fingerprint).