Tensile strength on friction stir processed AMg5 (5083) aluminum alloy

Аннотация

The results of the tensile tests carried out both on AMg5 (5083) aluminum alloy samples base and those obtained using friction stir processing technique are reported. The tensile test samples have been prepared from the friction stir processed plates so that their tensile axis was parallel to the processing direction. The maximum tensile strength of the processed samples was 9% higher than of the base metal. The fractographic examination shows the presence of flat areas inherent of the brittle fracture in all three friction processed samples. The load-extension curves show that friction stir processing may suppress the serrated yielding.

Язык оригинала	Английский
Номер статьи	020027
Журнал	AIP Conference Proceedings
Том	1783
DOI	https://doi.org/10.1063/1.4966320
Состояние	Опубликовано - 10 ноя 2016
Событие	International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016 - Tomsk, Российская Федерация Продолжительность: 19 сен 2016 → 23 сен 2016

ASJC Scopus subject areas

Physics and Astronomy(all)

Доступ к документу

10.1063/1.4966320

Fingerprint Подробные сведения о темах исследования «Tensile strength on friction stir processed AMg5 (5083) aluminum alloy». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать

Tensile strength on friction stir processed AMg5 (5083) aluminum alloy. / Chumaevsky, A. V.; Eliseev, A. A.; Filippov, Andrey Vladimirovich; Rubtsov, V. E.; Tarasov, S. Yu.

В: AIP Conference Proceedings, Том 1783, 020027, 10.11.2016.

Результат исследований: Материалы для журнала › Статья › рецензирование

@article{ee8df260caab487cb44a8ca46739c74c,

title = "Tensile strength on friction stir processed AMg5 (5083) aluminum alloy",

abstract = "The results of the tensile tests carried out both on AMg5 (5083) aluminum alloy samples base and those obtained using friction stir processing technique are reported. The tensile test samples have been prepared from the friction stir processed plates so that their tensile axis was parallel to the processing direction. The maximum tensile strength of the processed samples was 9% higher than of the base metal. The fractographic examination shows the presence of flat areas inherent of the brittle fracture in all three friction processed samples. The load-extension curves show that friction stir processing may suppress the serrated yielding.",

author = "Chumaevsky, {A. V.} and Eliseev, {A. A.} and Filippov, {Andrey Vladimirovich} and Rubtsov, {V. E.} and Tarasov, {S. Yu}",

year = "2016",

month = nov,

day = "10",

doi = "10.1063/1.4966320",

language = "English",

volume = "1783",

journal = "AIP Conference Proceedings",

issn = "0094-243X",

publisher = "American Institute of Physics Publising LLC",

note = "International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016 ; Conference date: 19-09-2016 Through 23-09-2016",

}

TY - JOUR

T1 - Tensile strength on friction stir processed AMg5 (5083) aluminum alloy

AU - Chumaevsky, A. V.

AU - Eliseev, A. A.

AU - Filippov, Andrey Vladimirovich

AU - Rubtsov, V. E.

AU - Tarasov, S. Yu

PY - 2016/11/10

Y1 - 2016/11/10

N2 - The results of the tensile tests carried out both on AMg5 (5083) aluminum alloy samples base and those obtained using friction stir processing technique are reported. The tensile test samples have been prepared from the friction stir processed plates so that their tensile axis was parallel to the processing direction. The maximum tensile strength of the processed samples was 9% higher than of the base metal. The fractographic examination shows the presence of flat areas inherent of the brittle fracture in all three friction processed samples. The load-extension curves show that friction stir processing may suppress the serrated yielding.

AB - The results of the tensile tests carried out both on AMg5 (5083) aluminum alloy samples base and those obtained using friction stir processing technique are reported. The tensile test samples have been prepared from the friction stir processed plates so that their tensile axis was parallel to the processing direction. The maximum tensile strength of the processed samples was 9% higher than of the base metal. The fractographic examination shows the presence of flat areas inherent of the brittle fracture in all three friction processed samples. The load-extension curves show that friction stir processing may suppress the serrated yielding.

UR - http://www.scopus.com/inward/record.url?scp=85006043651&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85006043651&partnerID=8YFLogxK

U2 - 10.1063/1.4966320

DO - 10.1063/1.4966320

M3 - Article

AN - SCOPUS:85006043651

VL - 1783

JO - AIP Conference Proceedings

JF - AIP Conference Proceedings

SN - 0094-243X

M1 - 020027

T2 - International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016

Y2 - 19 September 2016 through 23 September 2016

ER -