Synthesis of Spinel from Caustic Magnesite and Alumina Dust

I. D. Kashcheev, V. A. Kamenskikh, K. G. Zemlyanoi, O. F. Shatilov, V. N. Koptelov, D. V. Ponomarev

Результат исследований: Материалы для журналаСтатьярецензирование

3 Цитирования (Scopus)

Аннотация

The sintering of a mixture of a caustic dust and an alumina dust collected from electric filters taken in MgO/Al2O3 ratios of 0.1, 0.28, 0.5, and 0.75 at 1650°C is studied. Materials with superior physicomechanical properties are obtained: open porosity, 1.2 – 8.4%; density, more than 3.5 g/cm3, and compressive strength, 160 – 410 MPa. High-density pellets (free of additions) are prepared at a MgO/Al2O3 ratio of 0.75, with compressive strength as high as 160 MPa.

Язык оригиналаАнглийский
Страницы (с-по)301-305
Число страниц5
ЖурналRefractories and Industrial Ceramics
Том44
Номер выпуска5
DOI
СостояниеОпубликовано - 1 сен 2003
Опубликовано для внешнего пользованияДа

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

Fingerprint Подробные сведения о темах исследования «Synthesis of Spinel from Caustic Magnesite and Alumina Dust». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать