Surface modification of Ti6Al4V alloy scaffolds manufactured by electron beam melting

E. Chudinova, M. Surmeneva, A. Koptyug, K. Loza, O. Prymak, M. Epple, R. Surmenev

Результат исследований: Материалы для журналарецензирование

2 Цитирования (Scopus)


In this paper, the results of the surface functionalization of the Ti6Al4V alloy scaffolds with different structures for use as a material for medical implants are presented. Radio frequency magnetron sputtering was used to modify the surface of the porous structures by deposition of the biocompatible hydroxyapatite (HA) coating with the thickness of 86050 nm. The surface morphology, elemental and phase composition of the HA-coated scaffolds were studied. According to energy-dispersive X-ray spectroscopy, the stoichiometric ratio of Ca/P for flat, orthorhombic and cubic scaffolds is 1.65, 1.60, 1.53, respectively, which is close to that of stoichiometric ratio for HA (Ca/P = 1.67). It was revealed that this method of deposition makes it possible to obtain the homogeneous crystalline coating both on the dense sample and in the case of scaffolds of complex geometry with different lattice cell structure.

Язык оригиналаАнглийский
Номер статьи012030
ЖурналJournal of Physics: Conference Series
Номер выпуска1
СостояниеОпубликовано - 9 янв 2019
Событие15th International Conference of Students and Young Scientists on Prospects of Fundamental Sciences Development, PFSD 2018 - Tomsk, Российская Федерация
Продолжительность: 24 апр 201827 апр 2018

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Подробные сведения о темах исследования «Surface modification of Ti6Al4V alloy scaffolds manufactured by electron beam melting». Вместе они формируют уникальный семантический отпечаток (fingerprint).