Study on detection limit of buried defects in concrete structures by using infrared thermography

Arao Kamoi, Yosizo Okamoto, Vladimir Vavilov

Результат исследований: Материалы для журналаСтатья

2 Цитирования (Scopus)

Выдержка

In Japan it happens that concrete parts suddenly collapse to create obstacles to the traffic in tunnels, on highways and bridges. Thus, the safety issue has become a serious social problem. Therefore, the detection of hidden defects in concrete building constructions in order to prevent an accidental damage is the important application area for nondestructive testing (NDT) techniques. Until now, the inspection is typically performed by using a hammer that is subjective and takes too much time. Infrared thermography is a promising NDT technique that might help in the fast detection of invisible (hidden) defects. Transient, or active, thermal NDT requires external thermal stimulation of the objects under test by warming up or cooling down the object surface. However, low-power and long heating is significantly affected by environmental conditions. Recent Japanese research in this area has been rather qualitative, i.e. without putting the accent on evaluating parameters of hidden defects. In this study, the experimental results are modeled and processed by using the thermal NDT software package developed at the Tomsk Institute of Introscopy. This has allowed not only optimizing test parameters but also obtaining reasonable estimates of defect parameters for air-filled voids and inclusions in concrete. It is shown that MRTD values measured by ourselves for the first time are of a little help while evaluating detection limit.

Язык оригиналаАнглийский
Страницы (с-по)1549-1555
Число страниц7
ЖурналKey Engineering Materials
Том270-273
Номер выпускаII
СостояниеОпубликовано - 2004

Отпечаток

Nondestructive examination
Concrete construction
Defects
Concretes
Concrete buildings
Sodium Glutamate
Hammers
Software packages
Tunnels
Inspection
Cooling
Heating
Air
Hot Temperature

ASJC Scopus subject areas

  • Ceramics and Composites
  • Chemical Engineering (miscellaneous)

Цитировать

Study on detection limit of buried defects in concrete structures by using infrared thermography. / Kamoi, Arao; Okamoto, Yosizo; Vavilov, Vladimir.

В: Key Engineering Materials, Том 270-273, № II, 2004, стр. 1549-1555.

Результат исследований: Материалы для журналаСтатья

@article{d04d690e107a4318a421495a277d2088,
title = "Study on detection limit of buried defects in concrete structures by using infrared thermography",
abstract = "In Japan it happens that concrete parts suddenly collapse to create obstacles to the traffic in tunnels, on highways and bridges. Thus, the safety issue has become a serious social problem. Therefore, the detection of hidden defects in concrete building constructions in order to prevent an accidental damage is the important application area for nondestructive testing (NDT) techniques. Until now, the inspection is typically performed by using a hammer that is subjective and takes too much time. Infrared thermography is a promising NDT technique that might help in the fast detection of invisible (hidden) defects. Transient, or active, thermal NDT requires external thermal stimulation of the objects under test by warming up or cooling down the object surface. However, low-power and long heating is significantly affected by environmental conditions. Recent Japanese research in this area has been rather qualitative, i.e. without putting the accent on evaluating parameters of hidden defects. In this study, the experimental results are modeled and processed by using the thermal NDT software package developed at the Tomsk Institute of Introscopy. This has allowed not only optimizing test parameters but also obtaining reasonable estimates of defect parameters for air-filled voids and inclusions in concrete. It is shown that MRTD values measured by ourselves for the first time are of a little help while evaluating detection limit.",
keywords = "Buried defects, Concrete structures, Detection limit, Health monitoring, Infrared radiometer, Infrared thermography, MRTD",
author = "Arao Kamoi and Yosizo Okamoto and Vladimir Vavilov",
year = "2004",
language = "English",
volume = "270-273",
pages = "1549--1555",
journal = "Key Engineering Materials",
issn = "1013-9826",
publisher = "Trans Tech Publications",
number = "II",

}

TY - JOUR

T1 - Study on detection limit of buried defects in concrete structures by using infrared thermography

AU - Kamoi, Arao

AU - Okamoto, Yosizo

AU - Vavilov, Vladimir

PY - 2004

Y1 - 2004

N2 - In Japan it happens that concrete parts suddenly collapse to create obstacles to the traffic in tunnels, on highways and bridges. Thus, the safety issue has become a serious social problem. Therefore, the detection of hidden defects in concrete building constructions in order to prevent an accidental damage is the important application area for nondestructive testing (NDT) techniques. Until now, the inspection is typically performed by using a hammer that is subjective and takes too much time. Infrared thermography is a promising NDT technique that might help in the fast detection of invisible (hidden) defects. Transient, or active, thermal NDT requires external thermal stimulation of the objects under test by warming up or cooling down the object surface. However, low-power and long heating is significantly affected by environmental conditions. Recent Japanese research in this area has been rather qualitative, i.e. without putting the accent on evaluating parameters of hidden defects. In this study, the experimental results are modeled and processed by using the thermal NDT software package developed at the Tomsk Institute of Introscopy. This has allowed not only optimizing test parameters but also obtaining reasonable estimates of defect parameters for air-filled voids and inclusions in concrete. It is shown that MRTD values measured by ourselves for the first time are of a little help while evaluating detection limit.

AB - In Japan it happens that concrete parts suddenly collapse to create obstacles to the traffic in tunnels, on highways and bridges. Thus, the safety issue has become a serious social problem. Therefore, the detection of hidden defects in concrete building constructions in order to prevent an accidental damage is the important application area for nondestructive testing (NDT) techniques. Until now, the inspection is typically performed by using a hammer that is subjective and takes too much time. Infrared thermography is a promising NDT technique that might help in the fast detection of invisible (hidden) defects. Transient, or active, thermal NDT requires external thermal stimulation of the objects under test by warming up or cooling down the object surface. However, low-power and long heating is significantly affected by environmental conditions. Recent Japanese research in this area has been rather qualitative, i.e. without putting the accent on evaluating parameters of hidden defects. In this study, the experimental results are modeled and processed by using the thermal NDT software package developed at the Tomsk Institute of Introscopy. This has allowed not only optimizing test parameters but also obtaining reasonable estimates of defect parameters for air-filled voids and inclusions in concrete. It is shown that MRTD values measured by ourselves for the first time are of a little help while evaluating detection limit.

KW - Buried defects

KW - Concrete structures

KW - Detection limit

KW - Health monitoring

KW - Infrared radiometer

KW - Infrared thermography

KW - MRTD

UR - http://www.scopus.com/inward/record.url?scp=8644290821&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=8644290821&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:8644290821

VL - 270-273

SP - 1549

EP - 1555

JO - Key Engineering Materials

JF - Key Engineering Materials

SN - 1013-9826

IS - II

ER -