Structure-phase states of silumin surface layer after electron beam and high cycle fatigue

Modification of eutectic silumin surface has been implemented by high-intensity pulsed electron beam. The irradiation mode has been revealed; it allows increasing silumin fatigue life in more than 3.5 times. It has been established that the main reason of this fact is the formation of a multiphase submicro- and nanosized structure. It has been elicited that the most danger stress concentrators are large silicon plates situated on the surface and near-surface layers.