Structure, mechanical, and tribotechnical properties of an austenitic nitrogen steel after frictional treatment

N. A. Narkevich, I. A. Shulepov, Yu P. Mironov

    Результат исследований: Материалы для журналаСтатья

    2 Цитирования (Scopus)

    Выдержка

    The features of the structure and the mechanical and tribotechnical properties of an austenitic nitrogen steel (Cr16.5, Mn18.8, C0.07, N0.53, Si0.52 wt %, and Fe for balance) after frictional treatment have been studied. It has been shown that, along with twinning, the nitrogen austenite upon frictional treatment undergoes a γ → stacking fault → ε transformation. The strengthening of the steel by the frictional treatment manifests in a delay of the onset of the plastic flow. In the structure of the surface layer with a thickness of 5 μm, a high concentration of stacking faults has been detected. The mechanical properties depend on the orientation of the acting stresses relative to the direction of the frictional treatment. Upon the sliding friction of a ball made of hard alloy (94%WC + 6%Co) on the strengthened surface, an anomalously low coefficient of friction of 0.13 is observed. The coefficient of friction in the presence of abrasive particles in the form of wear debris increases to 0.50; however, the wear rate is almost two times lower compared to the same characteristic for a nonstrengthened surface of the nitrogen steel tested under the same conditions.

    Язык оригиналаАнглийский
    Страницы (с-по)399-406
    Число страниц8
    ЖурналPhysics of Metals and Metallography
    Том118
    Номер выпуска4
    DOI
    СостояниеОпубликовано - 1 апр 2017

    Отпечаток

    Steel
    Nitrogen
    Stacking faults
    steels
    mechanical properties
    Friction
    nitrogen
    Wear of materials
    crystal defects
    coefficient of friction
    Twinning
    Plastic flow
    Abrasives
    Debris
    sliding friction
    Austenite
    plastic flow
    abrasives
    twinning
    austenite

    ASJC Scopus subject areas

    • Condensed Matter Physics
    • Materials Chemistry

    Цитировать

    Structure, mechanical, and tribotechnical properties of an austenitic nitrogen steel after frictional treatment. / Narkevich, N. A.; Shulepov, I. A.; Mironov, Yu P.

    В: Physics of Metals and Metallography, Том 118, № 4, 01.04.2017, стр. 399-406.

    Результат исследований: Материалы для журналаСтатья

    Narkevich, N. A. ; Shulepov, I. A. ; Mironov, Yu P. / Structure, mechanical, and tribotechnical properties of an austenitic nitrogen steel after frictional treatment. В: Physics of Metals and Metallography. 2017 ; Том 118, № 4. стр. 399-406.
    @article{7c38d8d63eb9483a9fa9b836094485e2,
    title = "Structure, mechanical, and tribotechnical properties of an austenitic nitrogen steel after frictional treatment",
    abstract = "The features of the structure and the mechanical and tribotechnical properties of an austenitic nitrogen steel (Cr16.5, Mn18.8, C0.07, N0.53, Si0.52 wt {\%}, and Fe for balance) after frictional treatment have been studied. It has been shown that, along with twinning, the nitrogen austenite upon frictional treatment undergoes a γ → stacking fault → ε transformation. The strengthening of the steel by the frictional treatment manifests in a delay of the onset of the plastic flow. In the structure of the surface layer with a thickness of 5 μm, a high concentration of stacking faults has been detected. The mechanical properties depend on the orientation of the acting stresses relative to the direction of the frictional treatment. Upon the sliding friction of a ball made of hard alloy (94{\%}WC + 6{\%}Co) on the strengthened surface, an anomalously low coefficient of friction of 0.13 is observed. The coefficient of friction in the presence of abrasive particles in the form of wear debris increases to 0.50; however, the wear rate is almost two times lower compared to the same characteristic for a nonstrengthened surface of the nitrogen steel tested under the same conditions.",
    keywords = "frictional treatment, mechanical properties, nitrogen steel, stacking fault, tribotechnical properties, ε martensite",
    author = "Narkevich, {N. A.} and Shulepov, {I. A.} and Mironov, {Yu P.}",
    year = "2017",
    month = "4",
    day = "1",
    doi = "10.1134/S0031918X17020090",
    language = "English",
    volume = "118",
    pages = "399--406",
    journal = "Physics of Metals and Metallography",
    issn = "0031-918X",
    publisher = "Maik Nauka-Interperiodica Publishing",
    number = "4",

    }

    TY - JOUR

    T1 - Structure, mechanical, and tribotechnical properties of an austenitic nitrogen steel after frictional treatment

    AU - Narkevich, N. A.

    AU - Shulepov, I. A.

    AU - Mironov, Yu P.

    PY - 2017/4/1

    Y1 - 2017/4/1

    N2 - The features of the structure and the mechanical and tribotechnical properties of an austenitic nitrogen steel (Cr16.5, Mn18.8, C0.07, N0.53, Si0.52 wt %, and Fe for balance) after frictional treatment have been studied. It has been shown that, along with twinning, the nitrogen austenite upon frictional treatment undergoes a γ → stacking fault → ε transformation. The strengthening of the steel by the frictional treatment manifests in a delay of the onset of the plastic flow. In the structure of the surface layer with a thickness of 5 μm, a high concentration of stacking faults has been detected. The mechanical properties depend on the orientation of the acting stresses relative to the direction of the frictional treatment. Upon the sliding friction of a ball made of hard alloy (94%WC + 6%Co) on the strengthened surface, an anomalously low coefficient of friction of 0.13 is observed. The coefficient of friction in the presence of abrasive particles in the form of wear debris increases to 0.50; however, the wear rate is almost two times lower compared to the same characteristic for a nonstrengthened surface of the nitrogen steel tested under the same conditions.

    AB - The features of the structure and the mechanical and tribotechnical properties of an austenitic nitrogen steel (Cr16.5, Mn18.8, C0.07, N0.53, Si0.52 wt %, and Fe for balance) after frictional treatment have been studied. It has been shown that, along with twinning, the nitrogen austenite upon frictional treatment undergoes a γ → stacking fault → ε transformation. The strengthening of the steel by the frictional treatment manifests in a delay of the onset of the plastic flow. In the structure of the surface layer with a thickness of 5 μm, a high concentration of stacking faults has been detected. The mechanical properties depend on the orientation of the acting stresses relative to the direction of the frictional treatment. Upon the sliding friction of a ball made of hard alloy (94%WC + 6%Co) on the strengthened surface, an anomalously low coefficient of friction of 0.13 is observed. The coefficient of friction in the presence of abrasive particles in the form of wear debris increases to 0.50; however, the wear rate is almost two times lower compared to the same characteristic for a nonstrengthened surface of the nitrogen steel tested under the same conditions.

    KW - frictional treatment

    KW - mechanical properties

    KW - nitrogen steel

    KW - stacking fault

    KW - tribotechnical properties

    KW - ε martensite

    UR - http://www.scopus.com/inward/record.url?scp=85018724507&partnerID=8YFLogxK

    UR - http://www.scopus.com/inward/citedby.url?scp=85018724507&partnerID=8YFLogxK

    U2 - 10.1134/S0031918X17020090

    DO - 10.1134/S0031918X17020090

    M3 - Article

    AN - SCOPUS:85018724507

    VL - 118

    SP - 399

    EP - 406

    JO - Physics of Metals and Metallography

    JF - Physics of Metals and Metallography

    SN - 0031-918X

    IS - 4

    ER -