Structure and Properties of VT6 Alloy Obtained by Layered Selective Sintering of a Powder

A. D. Teresov, Yu F. Ivanov, E. A. Petrikova, N. N. Koval

Результат исследований: Материалы для журналаСтатья

Выдержка

This paper is focused on a clarification and analysis of the regularities of formation of the structure and properties of samples of the titanium-based alloy VT6, obtained by methods of conventional metallurgy and formed by layered selective electron-beam sintering in vacuum (using the Arcam A2X (3D printer) system (Arcam, Sweden)) of VT6 titanium powder with particle size 40–100 μm. Additional modification of the samples was realized by irradiating the surface with an intense pulsed electron beam (15 keV, 45 J/cm2, 200 μs, 10 pulses, 0.3 s–1, 3.5·10–2 Pa). It is shown that the action of a pulsed electron beam on the surface of samples formed by layered selective electron-beam sintering leads to a significant reduction in the porosity of the surface layer of the material and formation in the surface layer of a polycrystalline structure (grain size 15–60 μm) with a substructure in the form of crystallization cells (cell size 0.5–1.2 μm). Electron-beam processing of samples prepared by methods of conventional metallurgy for the indicated electron-beam parameters leads to the formation in the surface layer of a polycrystalline structure (grain size 50–800 μm) with a laminar intragrain substructure. Mechanical tests, performed by stretching flat samples, showed that the highest combination of mechanical strength and plasticity is possessed by samples obtained by layered selective electron-beam sintering with subsequent irradiation by an intense pulsed electron beam.

Язык оригиналаАнглийский
Страницы (с-по)1367-1372
Число страниц6
ЖурналRussian Physics Journal
Том60
Номер выпуска8
DOI
СостояниеОпубликовано - 1 дек 2017

Отпечаток

sintering
electron beams
surface layers
metallurgy
substructures
titanium
grain size
printers
Sweden
cells
regularity
plastic properties
crystallization
porosity
vacuum
irradiation
pulses

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Цитировать

Structure and Properties of VT6 Alloy Obtained by Layered Selective Sintering of a Powder. / Teresov, A. D.; Ivanov, Yu F.; Petrikova, E. A.; Koval, N. N.

В: Russian Physics Journal, Том 60, № 8, 01.12.2017, стр. 1367-1372.

Результат исследований: Материалы для журналаСтатья

@article{f2efea9c0f334e47ba83ab2a93d5fcbc,
title = "Structure and Properties of VT6 Alloy Obtained by Layered Selective Sintering of a Powder",
abstract = "This paper is focused on a clarification and analysis of the regularities of formation of the structure and properties of samples of the titanium-based alloy VT6, obtained by methods of conventional metallurgy and formed by layered selective electron-beam sintering in vacuum (using the Arcam A2X (3D printer) system (Arcam, Sweden)) of VT6 titanium powder with particle size 40–100 μm. Additional modification of the samples was realized by irradiating the surface with an intense pulsed electron beam (15 keV, 45 J/cm2, 200 μs, 10 pulses, 0.3 s–1, 3.5·10–2 Pa). It is shown that the action of a pulsed electron beam on the surface of samples formed by layered selective electron-beam sintering leads to a significant reduction in the porosity of the surface layer of the material and formation in the surface layer of a polycrystalline structure (grain size 15–60 μm) with a substructure in the form of crystallization cells (cell size 0.5–1.2 μm). Electron-beam processing of samples prepared by methods of conventional metallurgy for the indicated electron-beam parameters leads to the formation in the surface layer of a polycrystalline structure (grain size 50–800 μm) with a laminar intragrain substructure. Mechanical tests, performed by stretching flat samples, showed that the highest combination of mechanical strength and plasticity is possessed by samples obtained by layered selective electron-beam sintering with subsequent irradiation by an intense pulsed electron beam.",
keywords = "additive technologies, intense pulsed electron beam, properties, titanium alloy",
author = "Teresov, {A. D.} and Ivanov, {Yu F.} and Petrikova, {E. A.} and Koval, {N. N.}",
year = "2017",
month = "12",
day = "1",
doi = "10.1007/s11182-017-1223-3",
language = "English",
volume = "60",
pages = "1367--1372",
journal = "Russian Physics Journal",
issn = "1064-8887",
publisher = "Consultants Bureau",
number = "8",

}

TY - JOUR

T1 - Structure and Properties of VT6 Alloy Obtained by Layered Selective Sintering of a Powder

AU - Teresov, A. D.

AU - Ivanov, Yu F.

AU - Petrikova, E. A.

AU - Koval, N. N.

PY - 2017/12/1

Y1 - 2017/12/1

N2 - This paper is focused on a clarification and analysis of the regularities of formation of the structure and properties of samples of the titanium-based alloy VT6, obtained by methods of conventional metallurgy and formed by layered selective electron-beam sintering in vacuum (using the Arcam A2X (3D printer) system (Arcam, Sweden)) of VT6 titanium powder with particle size 40–100 μm. Additional modification of the samples was realized by irradiating the surface with an intense pulsed electron beam (15 keV, 45 J/cm2, 200 μs, 10 pulses, 0.3 s–1, 3.5·10–2 Pa). It is shown that the action of a pulsed electron beam on the surface of samples formed by layered selective electron-beam sintering leads to a significant reduction in the porosity of the surface layer of the material and formation in the surface layer of a polycrystalline structure (grain size 15–60 μm) with a substructure in the form of crystallization cells (cell size 0.5–1.2 μm). Electron-beam processing of samples prepared by methods of conventional metallurgy for the indicated electron-beam parameters leads to the formation in the surface layer of a polycrystalline structure (grain size 50–800 μm) with a laminar intragrain substructure. Mechanical tests, performed by stretching flat samples, showed that the highest combination of mechanical strength and plasticity is possessed by samples obtained by layered selective electron-beam sintering with subsequent irradiation by an intense pulsed electron beam.

AB - This paper is focused on a clarification and analysis of the regularities of formation of the structure and properties of samples of the titanium-based alloy VT6, obtained by methods of conventional metallurgy and formed by layered selective electron-beam sintering in vacuum (using the Arcam A2X (3D printer) system (Arcam, Sweden)) of VT6 titanium powder with particle size 40–100 μm. Additional modification of the samples was realized by irradiating the surface with an intense pulsed electron beam (15 keV, 45 J/cm2, 200 μs, 10 pulses, 0.3 s–1, 3.5·10–2 Pa). It is shown that the action of a pulsed electron beam on the surface of samples formed by layered selective electron-beam sintering leads to a significant reduction in the porosity of the surface layer of the material and formation in the surface layer of a polycrystalline structure (grain size 15–60 μm) with a substructure in the form of crystallization cells (cell size 0.5–1.2 μm). Electron-beam processing of samples prepared by methods of conventional metallurgy for the indicated electron-beam parameters leads to the formation in the surface layer of a polycrystalline structure (grain size 50–800 μm) with a laminar intragrain substructure. Mechanical tests, performed by stretching flat samples, showed that the highest combination of mechanical strength and plasticity is possessed by samples obtained by layered selective electron-beam sintering with subsequent irradiation by an intense pulsed electron beam.

KW - additive technologies

KW - intense pulsed electron beam

KW - properties

KW - titanium alloy

UR - http://www.scopus.com/inward/record.url?scp=85035749485&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85035749485&partnerID=8YFLogxK

U2 - 10.1007/s11182-017-1223-3

DO - 10.1007/s11182-017-1223-3

M3 - Article

AN - SCOPUS:85035749485

VL - 60

SP - 1367

EP - 1372

JO - Russian Physics Journal

JF - Russian Physics Journal

SN - 1064-8887

IS - 8

ER -