The paper studied Fe-Ni alloys obtained by sintering from mixtures of powders. Powders with 30-40 wt. Ni were mixed with paraffin and wax binder and then pressed and sintered at 1300 °C during 1 hour. It has been shown that the face centered cubic lattice (γ-phase) and body centered cubic lattice (α-phase) are formed after sintering of powders mixture. The content of the α-phase decreases from 37 % to 2 % with increase of Ni concentration from 30 to 35 wt. % Ni in powders mixture. The average grain size of the γ-phase decreases from 26.5±12.3 μm to 18.3±9.1 μm, and porosity of samples increases from 13±1.4 % to 18.4±1.1 %.The lattice parameter of the γ-phase increases from 3.5849•10-10 m to 3.597•10-10 m and it corresponds to well-known invar alloys. The maximum value of the microhardness of sintered samples is 1.04±0.07 GPa. Thus, alloys obtained by sintering of Fe and Ni powder mixtures has an invar properties typical of cast alloys.
|Журнал||IOP Conference Series: Materials Science and Engineering|
|Состояние||Опубликовано - 27 ноя 2019|
|Событие||3rd International Scientific and Technical Conference on Materials, Technology and Equipment for the Development of the Arctic and Siberia, ARCTIC 2019 - Tomsk, Российская Федерация|
Продолжительность: 25 сен 2019 → 28 сен 2019
ASJC Scopus subject areas
- Materials Science(all)