Structure and phase composition behavior in multicycle fatique of quenched carbon steel

V. E. Gromov, O. V. Sosnin, Yu F. Ivanov, E. V. Kozlov

Результат исследования: Материалы для книги/типы отчетовМатериалы для конференции

Аннотация

The defect substructure and phase composition evolution of quenched 60GS2 (0,6%C, 1%Mn, 2%Si) steel are studied by transmission diffraction electron microscopy. Quenching the steel leads to the formation of a mixed packet-plate martensite structure containing around 8-10% residual austenite. The mean transverse dimensions of the plate and packet martensite crystals are 242±11 nm and 180±10 nm, respectively. Fatigue loading of steel with Ni=1,2·105 cycles leads to the formation of subgrains, whose relative content is around 44%. The mean size of the anisotropic subgrains is 1,150±0,025 μ. Increasing the number of loading cycles to N 2=1,46·105 (failure) increases the subgrain content to around 75% and increases their mean size to 1,70±0,03 μm. Within the subgrains, there is a tangled-network dislocational structure. The scalar dislocation density is 2,8·1010cm-2. Cementite particles are distributed along the subgrain boundaries and at their junctions, as a rule. At the intermediate stage of loading, the cementite particles take the form of layers, while the failured sample tends to have globular morphology. In the intermediate stage of fatigue loading Ni displacement of the largeangle grain boundaries is observed, indicating dynamic recrystallization of the material. This process is accompanied by the formation of regions characterized by high elastic stress fields and a large quantity of cementite particles at the boundary junctions. Increasing the number of loading cycles to around 1,46·105 is accompanied by further tempering of these volumes of the material, with the formation of a two-phase martensite-austenite structure. Repeated martensitic transformation is sometimes also observed in inhomogeneous packets. In this case, the newly formed martensite crystals lie parallel to the initial martensite crystals.

Язык оригиналаАнглийский
Заголовок главной публикацииAdvances in Heterogeneous Material Mechanics 2008 - Proceedings of the 2nd International Conference on Heterogeneous Material Mechanics, ICHMM 2008
Страницы434
Количество страниц1
Статус публикацииОпубликовано - 2008
СобытиеAdvances in Heterogeneous Material Mechanics 2008 - 2nd International Conference on Heterogeneous Material Mechanics, ICHMM 2008 - Huangshan, Китай
Длительность: 3 июн 20088 июн 2008

Другое

ДругоеAdvances in Heterogeneous Material Mechanics 2008 - 2nd International Conference on Heterogeneous Material Mechanics, ICHMM 2008
СтранаКитай
ГородHuangshan
Период3.6.088.6.08

    Fingerprint

ASJC Scopus subject areas

  • Materials Science (miscellaneous)
  • Materials Chemistry

Цитировать

Gromov, V. E., Sosnin, O. V., Ivanov, Y. F., & Kozlov, E. V. (2008). Structure and phase composition behavior in multicycle fatique of quenched carbon steel. В Advances in Heterogeneous Material Mechanics 2008 - Proceedings of the 2nd International Conference on Heterogeneous Material Mechanics, ICHMM 2008 (стр. 434)