Structure and electronic states of gold species in mordenites

I. Tuzovskaya, N. Bogdanchikova, A. Simakov, V. Gurin, A. Pestryakov, M. Avalos, M. H. Farías

Результат исследований: Материалы для журналаСтатья

64 Цитирования (Scopus)

Выдержка

Au-zeolites with SiO2/Al2O3 molar ratios 10 and 206 were prepared by ion exchange of the H-mordenites with [Au(NH3)4](NO3)3 complex solution followed by hydrogen reduction or calcination at different temperatures. The samples were characterized by UV-visible DRS, XPS, XRD, TEM and TPR in order to understand the effect of zeolite acidity and pretreatment conditions on formation of different gold states. Three kinds of gold species were observed in the samples: (1) Au3+cations, (2) partly reduced species with the diameter less than 1 nm assigned to charged clusters Aunδ + (with n proposed ≤8), suggested to be stabilized inside zeolite channels, and (3) Au0 nanoparticles with diameter varied within interval of 1.5-20 nm. The third type is located on the external surface of zeolite microcrystals. Aunδ + clusters were observed in as-prepared samples just after ion-exchange. Acid site strength did not change significantly amount of the clusters but influenced the electronic state of gold in these clusters and redox properties of gold cations. The contribution of the clusters was not changed significantly with temperature treatment even up to 500 °C. Au0 nanoparticles were formed by reduction of gold ions at temperatures starting from 50 to 200 °C depending on the medium of treatment and the molar ratio of the zeolite. The obtained results are important for understanding the effect of multiplicity of catalytically active gold species in CO oxidation.

Язык оригиналаАнглийский
Страницы (с-по)23-32
Число страниц10
ЖурналChemical Physics
Том338
Номер выпуска1
DOI
СостояниеОпубликовано - 10 сен 2007

Отпечаток

Zeolites
Electronic states
Gold
gold
electronics
Cations
Ion exchange
Nanoparticles
cations
nanoparticles
Microcrystals
ions
microcrystals
Carbon Monoxide
Acidity
acidity
zeolites
pretreatment
Calcination
roasting

ASJC Scopus subject areas

  • Physical and Theoretical Chemistry
  • Spectroscopy
  • Atomic and Molecular Physics, and Optics

Цитировать

Tuzovskaya, I., Bogdanchikova, N., Simakov, A., Gurin, V., Pestryakov, A., Avalos, M., & Farías, M. H. (2007). Structure and electronic states of gold species in mordenites. Chemical Physics, 338(1), 23-32. https://doi.org/10.1016/j.chemphys.2007.07.026

Structure and electronic states of gold species in mordenites. / Tuzovskaya, I.; Bogdanchikova, N.; Simakov, A.; Gurin, V.; Pestryakov, A.; Avalos, M.; Farías, M. H.

В: Chemical Physics, Том 338, № 1, 10.09.2007, стр. 23-32.

Результат исследований: Материалы для журналаСтатья

Tuzovskaya, I, Bogdanchikova, N, Simakov, A, Gurin, V, Pestryakov, A, Avalos, M & Farías, MH 2007, 'Structure and electronic states of gold species in mordenites', Chemical Physics, том. 338, № 1, стр. 23-32. https://doi.org/10.1016/j.chemphys.2007.07.026
Tuzovskaya I, Bogdanchikova N, Simakov A, Gurin V, Pestryakov A, Avalos M и соавт. Structure and electronic states of gold species in mordenites. Chemical Physics. 2007 Сент. 10;338(1):23-32. https://doi.org/10.1016/j.chemphys.2007.07.026
Tuzovskaya, I. ; Bogdanchikova, N. ; Simakov, A. ; Gurin, V. ; Pestryakov, A. ; Avalos, M. ; Farías, M. H. / Structure and electronic states of gold species in mordenites. В: Chemical Physics. 2007 ; Том 338, № 1. стр. 23-32.
@article{22a305dd5e4f4eff9eac09c4c19dd973,
title = "Structure and electronic states of gold species in mordenites",
abstract = "Au-zeolites with SiO2/Al2O3 molar ratios 10 and 206 were prepared by ion exchange of the H-mordenites with [Au(NH3)4](NO3)3 complex solution followed by hydrogen reduction or calcination at different temperatures. The samples were characterized by UV-visible DRS, XPS, XRD, TEM and TPR in order to understand the effect of zeolite acidity and pretreatment conditions on formation of different gold states. Three kinds of gold species were observed in the samples: (1) Au3+cations, (2) partly reduced species with the diameter less than 1 nm assigned to charged clusters Aunδ + (with n proposed ≤8), suggested to be stabilized inside zeolite channels, and (3) Au0 nanoparticles with diameter varied within interval of 1.5-20 nm. The third type is located on the external surface of zeolite microcrystals. Aunδ + clusters were observed in as-prepared samples just after ion-exchange. Acid site strength did not change significantly amount of the clusters but influenced the electronic state of gold in these clusters and redox properties of gold cations. The contribution of the clusters was not changed significantly with temperature treatment even up to 500 °C. Au0 nanoparticles were formed by reduction of gold ions at temperatures starting from 50 to 200 °C depending on the medium of treatment and the molar ratio of the zeolite. The obtained results are important for understanding the effect of multiplicity of catalytically active gold species in CO oxidation.",
keywords = "Clusters, Gold, Nanoparticles, Zeolite",
author = "I. Tuzovskaya and N. Bogdanchikova and A. Simakov and V. Gurin and A. Pestryakov and M. Avalos and Far{\'i}as, {M. H.}",
year = "2007",
month = "9",
day = "10",
doi = "10.1016/j.chemphys.2007.07.026",
language = "English",
volume = "338",
pages = "23--32",
journal = "Chemical Physics",
issn = "0301-0104",
publisher = "Elsevier",
number = "1",

}

TY - JOUR

T1 - Structure and electronic states of gold species in mordenites

AU - Tuzovskaya, I.

AU - Bogdanchikova, N.

AU - Simakov, A.

AU - Gurin, V.

AU - Pestryakov, A.

AU - Avalos, M.

AU - Farías, M. H.

PY - 2007/9/10

Y1 - 2007/9/10

N2 - Au-zeolites with SiO2/Al2O3 molar ratios 10 and 206 were prepared by ion exchange of the H-mordenites with [Au(NH3)4](NO3)3 complex solution followed by hydrogen reduction or calcination at different temperatures. The samples were characterized by UV-visible DRS, XPS, XRD, TEM and TPR in order to understand the effect of zeolite acidity and pretreatment conditions on formation of different gold states. Three kinds of gold species were observed in the samples: (1) Au3+cations, (2) partly reduced species with the diameter less than 1 nm assigned to charged clusters Aunδ + (with n proposed ≤8), suggested to be stabilized inside zeolite channels, and (3) Au0 nanoparticles with diameter varied within interval of 1.5-20 nm. The third type is located on the external surface of zeolite microcrystals. Aunδ + clusters were observed in as-prepared samples just after ion-exchange. Acid site strength did not change significantly amount of the clusters but influenced the electronic state of gold in these clusters and redox properties of gold cations. The contribution of the clusters was not changed significantly with temperature treatment even up to 500 °C. Au0 nanoparticles were formed by reduction of gold ions at temperatures starting from 50 to 200 °C depending on the medium of treatment and the molar ratio of the zeolite. The obtained results are important for understanding the effect of multiplicity of catalytically active gold species in CO oxidation.

AB - Au-zeolites with SiO2/Al2O3 molar ratios 10 and 206 were prepared by ion exchange of the H-mordenites with [Au(NH3)4](NO3)3 complex solution followed by hydrogen reduction or calcination at different temperatures. The samples were characterized by UV-visible DRS, XPS, XRD, TEM and TPR in order to understand the effect of zeolite acidity and pretreatment conditions on formation of different gold states. Three kinds of gold species were observed in the samples: (1) Au3+cations, (2) partly reduced species with the diameter less than 1 nm assigned to charged clusters Aunδ + (with n proposed ≤8), suggested to be stabilized inside zeolite channels, and (3) Au0 nanoparticles with diameter varied within interval of 1.5-20 nm. The third type is located on the external surface of zeolite microcrystals. Aunδ + clusters were observed in as-prepared samples just after ion-exchange. Acid site strength did not change significantly amount of the clusters but influenced the electronic state of gold in these clusters and redox properties of gold cations. The contribution of the clusters was not changed significantly with temperature treatment even up to 500 °C. Au0 nanoparticles were formed by reduction of gold ions at temperatures starting from 50 to 200 °C depending on the medium of treatment and the molar ratio of the zeolite. The obtained results are important for understanding the effect of multiplicity of catalytically active gold species in CO oxidation.

KW - Clusters

KW - Gold

KW - Nanoparticles

KW - Zeolite

UR - http://www.scopus.com/inward/record.url?scp=34548232808&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=34548232808&partnerID=8YFLogxK

U2 - 10.1016/j.chemphys.2007.07.026

DO - 10.1016/j.chemphys.2007.07.026

M3 - Article

AN - SCOPUS:34548232808

VL - 338

SP - 23

EP - 32

JO - Chemical Physics

JF - Chemical Physics

SN - 0301-0104

IS - 1

ER -