Structure and abrasive wear resistance of R6M5 steel-tungsten carbide composite coatings

Результат исследований: Материалы для журналаСтатья

1 Цитирования (Scopus)

Аннотация

Features of the structure formation, composition, and abrasive wear resistance of R6M5 steel-tungsten carbide (R6M5-WC) composite coatings have been studied as dependent on the WC content. The introduction of ~20 wt % WC into the hardening composition leads to an increase in the fraction of M 6C carbide (in the form of eutectic inclusions with average size ~5.9 μm at grain boundaries and dispersed ~0.25 μm particles in the volume of grains), while a large proportion of metastable austenite (~88 vol %) is still retained. The R6M5-WC coatings exhibit high abrasive wear resistance, which is ensured by the γ → α′ martensite transformation during friction and a muiltimodal size distribution of hardening particles.

Язык оригиналаАнглийский
Страницы (с-по)861-864
Число страниц4
ЖурналTechnical Physics Letters
Том38
Номер выпуска9
DOI
СостояниеОпубликовано - 17 окт 2012

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)

Fingerprint Подробные сведения о темах исследования «Structure and abrasive wear resistance of R6M5 steel-tungsten carbide composite coatings». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать