Structural defects in Tini-based alloys after warm ECAP

Aleksandr Lotkov, Anatoly Baturin, Vladimir Kopylov, Victor Grishkov, Roman Laptev

Результат исследований: Материалы для журналаСтатья

Аннотация

The microstructure, martensitic transformations and crystal structure defects in the Ti50Ni47.3Fe2.7 (at%) alloy after equal-channel angular pressing (ECAP, angle 90°, route BC, 1–3 passes at T = 723 K) have been investigated. A homogeneous submicrocrystalline (SMC) structure (grains / subgrains about 300 nm) is observed after 3 ECAP passes. Crystal structure defects in the Ti49.4Ni50.6 (at%) alloy (8 ECAP passes, angle 120°, BC route, T = 723 K, grains/subgrains about 300 nm) and Ti50Ni47.3Fe2.7 (at%) alloy with SMC B2 structures after ECAP were studied by positron lifetime spectroscopy at the room temperature. The single component with the positron lifetime τ1 = 132 ps and τ1 = 140 ps were observed for positron lifetime spectra (PLS) obtained from ternary and binary, correspondingly, annealed alloys with coarse-grained structures. This τ1 values correspond to the lifetime of delocalized positrons in defect-free B2 phase. The two component PLS were found for all samples exposed by ECAP. The component with τ2 = 160 ps (annihilation of positrons trapped by dislocations) is observed for all samples after 1–8 ECAP passes. The component with τ3 = 305 ps (annihilation of positrons trapped by vacancy nanoclusters) was detected only after the first ECAP pass. The component with τ3 = 200 ps (annihilation of positrons trapped by vacancies in the Ti sublattice of B2 structure) is observed for all samples after 3–8 ECAP passes.

Язык оригиналаАнглийский
Номер статьи1154
Страницы (с-по)1-12
Число страниц12
ЖурналMetals
Том10
Номер выпуска9
DOI
СостояниеОпубликовано - сен 2020

ASJC Scopus subject areas

  • Materials Science(all)

Fingerprint Подробные сведения о темах исследования «Structural defects in Tini-based alloys after warm ECAP». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать

    Lotkov, A., Baturin, A., Kopylov, V., Grishkov, V., & Laptev, R. (2020). Structural defects in Tini-based alloys after warm ECAP. Metals, 10(9), 1-12. [1154]. https://doi.org/10.3390/met10091154