Solid nanocrystalline fullerite-containing carbon coatings

K. V. Oskomov, N. S. Sochugov, A. A. Solov'ev, S. V. Rabotkin

Результат исследований: Материалы для журналаСтатья

5 Цитирования (Scopus)

Аннотация

Solid carbon coatings with a high content of nanocrystalline fullerite have been obtained using unbalanced magnetron sputtering of graphite under conditions of pulsed high-voltage ion bombardment of the film growing on a substrate. It is established that samples possessing the maximum hardness (18.8 GPa) are characterized by maximum values of the volume fraction of fullerite in the coating (50%), coherent scattering domain size (53 nm), degree of preferred grain orientation (85%), relative deformation of the lattice (1.02%), and internal compressive stresses (2.91 GPa). The observed behavior is consistent with the mechanism of strengthening that accounts for the phenomenon of superhardness in nanocrystalline and nanocomposite materials. This assumption is confirmed by the results of investigation of the morphology of growing coatings.

Язык оригиналаАнглийский
Страницы (с-по)889-892
Число страниц4
ЖурналTechnical Physics Letters
Том35
Номер выпуска10
DOI
СостояниеОпубликовано - 27 ноя 2009

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)

Fingerprint Подробные сведения о темах исследования «Solid nanocrystalline fullerite-containing carbon coatings». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать