Shear bands and fracture of imperfect Fe+3%Si polycrystals

V. E. Panin, Ye Ye Derjugin, G. I. Wasman

Результат исследований: Материалы для журналаСтатьярецензирование

9 Цитирования (Scopus)

Аннотация

Experimental data on shear macrobands and fracture of flat specimens of Fe+3%Si alloy having only a few grains in a cross-section are analyzed. Four types of band structures that determine the stress-strain curves involving different loading behavior and ductility of the alloy are singled out. The lowest plasticity and strength are exhibited when a singular shear macroband is formed on the front face of a specimen at an angle of 45° to the axis of tension (p = 3-4%). Formation of a dipole out of two intersecting macrobands on the lateral surface of a specimen increases plasticity (p = 6-7%). Accommodation bands between the macrobands of the dipole increase the plasticity even more (p = 9-11%). It is the highest (p = 19-21%) when the flat grains filling up all of the specimen's cross-section are contained between smaller-sized grains. Ductile fracture of such a specimen is governed by coupling of the conjugate macrobands that interact via a mechanism of auto-oscillations.

Язык оригиналаАнглийский
Страницы (с-по)1-10
Число страниц10
ЖурналInternational Journal of Fracture
Том107
Номер выпуска1
DOI
СостояниеОпубликовано - янв 2001

ASJC Scopus subject areas

  • Computational Mechanics
  • Mechanics of Materials

Fingerprint Подробные сведения о темах исследования «Shear bands and fracture of imperfect Fe+3%Si polycrystals». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать