Relaxation capacity and cracking resistance of nitrous coating produced by electron-beam facing of 0.6C–24Cr–0.7N–16Mn steel powder during wear by hard abrasive under heavy loads

D. N. Tagiltseva, N. A. Narkevich, I. A. Shulepov, D. D. Moiseenko

    Результат исследований: Материалы для журналаСтатья

    2 Цитирования (Scopus)

    Аннотация

    Specific features of the topography of friction tracks formed during the sliding of a WCo6 ball over an austenitic nitrous coating at various velocities of sliding under various loads using the ball-on-disc arrangement are studied and compared with those for the WCo6 ball–110Mn13 steel pair. It has been found that the wear resistance of nitrous austenite is due to its capacity to relax frictional stresses. The correlation between the H3/E2 parameter of the friction surface and the wear rate has been shown.

    Язык оригиналаАнглийский
    Страницы (с-по)104-110
    Число страниц7
    ЖурналJournal of Friction and Wear
    Том35
    Номер выпуска2
    DOI
    СостояниеОпубликовано - 1 янв 2014

    ASJC Scopus subject areas

    • Mechanics of Materials
    • Surfaces, Coatings and Films

    Fingerprint Подробные сведения о темах исследования «Relaxation capacity and cracking resistance of nitrous coating produced by electron-beam facing of 0.6C–24Cr–0.7N–16Mn steel powder during wear by hard abrasive under heavy loads». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать