Relationships between hardness, Young's modulus and elastic recovery in hard nanocomposite coatings

J. Musil, F. Kunc, H. Zeman, H. Poláková

Результат исследований: Материалы для журналаСтатьярецензирование

421 Цитирования (Scopus)

Аннотация

The paper is devoted to an assessment of the mechanical behavior of hard and superhard nanocomposite coatings from loading/ unloading curves measured by a computer-controlled Fischerscope H 100 microhardness tester and a maximum depth dmax of the diamond indenter impression into the coating at a given load L. It is shown that: (1) the area between the loading/unloading curve and the value of dmax decreases with increasing (i) hardness H, (ii) effective Young's modulus E =E/(1-v2) and (iii) universal hardness HU, where E and v are the Young's modulus and the Poisson ratio, respectively; and (2) there is no simple relation between the mechanical response of the coating and H or E alone; however, this response is strongly dependent on the ratio H/E. The last fact gives a possibility of tailoring the mechanical properties of a coating for a given application, e.g. to prepare coatings with high hardness H, high resistance to plastic deformation (ΟH3 /E2), high elastic recovery Wc, but with low E and high dmax. Special attention is also given to the analysis of problems in accurately measuring the hardness of superhard (≥60 GPa) coatings. It is shown that a high elastic recovery Wc≥80% of superhard films with H≥60 GPa (1) strongly decreases the gradient dH/dL and (2) shifts the region L, where H(L) ≈ constant and the hardness H is correctly measured, to higher values of L. This means that the lowest load L used in the hardness measurement must be higher than L used in measurements of coatings with H<60 GPa to prevent the value of H measured from being significantly higher than the real hardness of the coating.

Язык оригиналаАнглийский
Страницы (с-по)304-313
Число страниц10
ЖурналSurface and Coatings Technology
Том154
Номер выпуска2-3
DOI
СостояниеОпубликовано - 15 мая 2002

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

Fingerprint Подробные сведения о темах исследования «Relationships between hardness, Young's modulus and elastic recovery in hard nanocomposite coatings». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать