Pulsed electron-beam melting of high-speed steel: Structural phase transformations and wear resistance

Yu Ivanov, W. Matz, V. Rotshtein, R. Günzel, N. Shevchenko

Результат исследований: Материалы для журналаСтатьярецензирование

76 Цитирования (Scopus)


The structural and phase transformations occurring in the near-surface layers of pre-quenched high-speed steel subjected to pulsed electron beam melting have been investigated. Melting was induced by a low-energy (20-30 keV), high-current electron beam with a pulse duration of 2.5 μms and an energy density ranging from 3 to 18 J/cm2. Using electron microscopy and X-ray diffraction it has been revealed that with increasing beam energy density gradual liquid-phase dissolution of initial globular M6C carbide particles occurs in the near-surface layer of thickness up to ∼ 1 μm. This process is accompanied by the formation of martensite crystals (α-phase) and an increase of residual austenite (γ-phase) content. When the carbide particles are completely dissolved, martensitic transformation is suppressed. In this case, a non-misoriented structure is formed consisting predominantly of submicrometer cells of γ-phase separated by nanosized carbide interlayers. Irradiation of cutting tools (drills) in a mode corresponding to an abrupt decrease in the content of M6C particles due to their liquid-phase dissolution enhances the wear resistance of the drills by a factor of 1.7. This is associated with the fixation of undissolved particles in the matrix, the formation of residual compressive stresses and of dispersed M3C carbide particles as well as the high (∼ 50%) content of the metastable γ-phase in the surface layer.

Язык оригиналаАнглийский
Страницы (с-по)188-198
Число страниц11
ЖурналSurface and Coatings Technology
Номер выпуска2-3
СостояниеОпубликовано - 15 фев 2002

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

Fingerprint Подробные сведения о темах исследования «Pulsed electron-beam melting of high-speed steel: Structural phase transformations and wear resistance». Вместе они формируют уникальный семантический отпечаток (fingerprint).