Porosity and mechanical properties of zirconium ceramics

S. Buyakova, T. Sablina, S. Kulkov

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

4 Цитирования (Scopus)

Выдержка

Has been studied a porous ceramics obtained from ultra-fine powders. Porous ceramic ZrO2(MgO), ZrO2(Y2O3) powder was prepared by pressing and subsequent sintering of compacts homologous temperatures ranging from 0.63 to 0.56 during the isothermal holding duration of 1 to 5 hours. The porosity of ceramic samples was from 15 to 80%. The structure of the ceramic materials produced from plasma-sprayed ZrO2 powder was represented as a system of cell and rod structure elements. Cellular structure formed by stacking hollow powder particles can be easily seen at the images of fracture surfaces of obtained ceramics. There were three types of pores in ceramics: large cellular hollow spaces, small interparticle pores which are not filled with powder particles and the smallest pores in the shells of cells. The cells generally did not have regular shapes. The size of the interior of the cells many times exceeded the thickness of the walls which was a single-layer packing of ZrO2 grains. A distinctive feature of all deformation diagrams obtained in the experiment was their nonlinearity at low deformations which was described by the parabolic law. It was shown that the observed nonlinear elasticity for low deformation on deformation diagrams is due to mechanical instability of the cellular elements in the ceramic carcass.

Язык оригиналаАнглийский
Название основной публикацииNew Operational Technologies, NEWOT 2015
Подзаголовок основной публикацииProceedings of the 5th International Scientific Conference "New Operational Technologies"
РедакторыYury V. Kistenev, Yurii P. Sharkeev, Mikhail A. Sadovoy, Sergei N. Orlov
ИздательAmerican Institute of Physics Inc.
Том1688
ISBN (электронное издание)9780735413351
DOI
СостояниеОпубликовано - 17 ноя 2015
Событие5th International Scientific Conference on New Operational Technologies, NEWOT 2015 - Tomsk, Российская Федерация
Продолжительность: 29 сен 201530 сен 2015

Конференция

Конференция5th International Scientific Conference on New Operational Technologies, NEWOT 2015
СтранаРоссийская Федерация
ГородTomsk
Период29.9.1530.9.15

Отпечаток

mechanical properties
ceramics
porosity
cells
hollow
diagrams
pressing
sintering
rods
elastic properties
nonlinearity
temperature

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Цитировать

Buyakova, S., Sablina, T., & Kulkov, S. (2015). Porosity and mechanical properties of zirconium ceramics. В Y. V. Kistenev, Y. P. Sharkeev, M. A. Sadovoy, & S. N. Orlov (Ред.), New Operational Technologies, NEWOT 2015: Proceedings of the 5th International Scientific Conference "New Operational Technologies" (Том 1688). [030009] American Institute of Physics Inc.. https://doi.org/10.1063/1.4936004

Porosity and mechanical properties of zirconium ceramics. / Buyakova, S.; Sablina, T.; Kulkov, S.

New Operational Technologies, NEWOT 2015: Proceedings of the 5th International Scientific Conference "New Operational Technologies". ред. / Yury V. Kistenev; Yurii P. Sharkeev; Mikhail A. Sadovoy; Sergei N. Orlov. Том 1688 American Institute of Physics Inc., 2015. 030009.

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

Buyakova, S, Sablina, T & Kulkov, S 2015, Porosity and mechanical properties of zirconium ceramics. в YV Kistenev, YP Sharkeev, MA Sadovoy & SN Orlov (ред.), New Operational Technologies, NEWOT 2015: Proceedings of the 5th International Scientific Conference "New Operational Technologies". том. 1688, 030009, American Institute of Physics Inc., Tomsk, Российская Федерация, 29.9.15. https://doi.org/10.1063/1.4936004
Buyakova S, Sablina T, Kulkov S. Porosity and mechanical properties of zirconium ceramics. В Kistenev YV, Sharkeev YP, Sadovoy MA, Orlov SN, редакторы, New Operational Technologies, NEWOT 2015: Proceedings of the 5th International Scientific Conference "New Operational Technologies". Том 1688. American Institute of Physics Inc. 2015. 030009 https://doi.org/10.1063/1.4936004
Buyakova, S. ; Sablina, T. ; Kulkov, S. / Porosity and mechanical properties of zirconium ceramics. New Operational Technologies, NEWOT 2015: Proceedings of the 5th International Scientific Conference "New Operational Technologies". редактор / Yury V. Kistenev ; Yurii P. Sharkeev ; Mikhail A. Sadovoy ; Sergei N. Orlov. Том 1688 American Institute of Physics Inc., 2015.
@inproceedings{86077ab693594fb6aacaa4ae357ccfb8,
title = "Porosity and mechanical properties of zirconium ceramics",
abstract = "Has been studied a porous ceramics obtained from ultra-fine powders. Porous ceramic ZrO2(MgO), ZrO2(Y2O3) powder was prepared by pressing and subsequent sintering of compacts homologous temperatures ranging from 0.63 to 0.56 during the isothermal holding duration of 1 to 5 hours. The porosity of ceramic samples was from 15 to 80{\%}. The structure of the ceramic materials produced from plasma-sprayed ZrO2 powder was represented as a system of cell and rod structure elements. Cellular structure formed by stacking hollow powder particles can be easily seen at the images of fracture surfaces of obtained ceramics. There were three types of pores in ceramics: large cellular hollow spaces, small interparticle pores which are not filled with powder particles and the smallest pores in the shells of cells. The cells generally did not have regular shapes. The size of the interior of the cells many times exceeded the thickness of the walls which was a single-layer packing of ZrO2 grains. A distinctive feature of all deformation diagrams obtained in the experiment was their nonlinearity at low deformations which was described by the parabolic law. It was shown that the observed nonlinear elasticity for low deformation on deformation diagrams is due to mechanical instability of the cellular elements in the ceramic carcass.",
author = "S. Buyakova and T. Sablina and S. Kulkov",
year = "2015",
month = "11",
day = "17",
doi = "10.1063/1.4936004",
language = "English",
volume = "1688",
editor = "Kistenev, {Yury V.} and Sharkeev, {Yurii P.} and Sadovoy, {Mikhail A.} and Orlov, {Sergei N.}",
booktitle = "New Operational Technologies, NEWOT 2015",
publisher = "American Institute of Physics Inc.",

}

TY - GEN

T1 - Porosity and mechanical properties of zirconium ceramics

AU - Buyakova, S.

AU - Sablina, T.

AU - Kulkov, S.

PY - 2015/11/17

Y1 - 2015/11/17

N2 - Has been studied a porous ceramics obtained from ultra-fine powders. Porous ceramic ZrO2(MgO), ZrO2(Y2O3) powder was prepared by pressing and subsequent sintering of compacts homologous temperatures ranging from 0.63 to 0.56 during the isothermal holding duration of 1 to 5 hours. The porosity of ceramic samples was from 15 to 80%. The structure of the ceramic materials produced from plasma-sprayed ZrO2 powder was represented as a system of cell and rod structure elements. Cellular structure formed by stacking hollow powder particles can be easily seen at the images of fracture surfaces of obtained ceramics. There were three types of pores in ceramics: large cellular hollow spaces, small interparticle pores which are not filled with powder particles and the smallest pores in the shells of cells. The cells generally did not have regular shapes. The size of the interior of the cells many times exceeded the thickness of the walls which was a single-layer packing of ZrO2 grains. A distinctive feature of all deformation diagrams obtained in the experiment was their nonlinearity at low deformations which was described by the parabolic law. It was shown that the observed nonlinear elasticity for low deformation on deformation diagrams is due to mechanical instability of the cellular elements in the ceramic carcass.

AB - Has been studied a porous ceramics obtained from ultra-fine powders. Porous ceramic ZrO2(MgO), ZrO2(Y2O3) powder was prepared by pressing and subsequent sintering of compacts homologous temperatures ranging from 0.63 to 0.56 during the isothermal holding duration of 1 to 5 hours. The porosity of ceramic samples was from 15 to 80%. The structure of the ceramic materials produced from plasma-sprayed ZrO2 powder was represented as a system of cell and rod structure elements. Cellular structure formed by stacking hollow powder particles can be easily seen at the images of fracture surfaces of obtained ceramics. There were three types of pores in ceramics: large cellular hollow spaces, small interparticle pores which are not filled with powder particles and the smallest pores in the shells of cells. The cells generally did not have regular shapes. The size of the interior of the cells many times exceeded the thickness of the walls which was a single-layer packing of ZrO2 grains. A distinctive feature of all deformation diagrams obtained in the experiment was their nonlinearity at low deformations which was described by the parabolic law. It was shown that the observed nonlinear elasticity for low deformation on deformation diagrams is due to mechanical instability of the cellular elements in the ceramic carcass.

UR - http://www.scopus.com/inward/record.url?scp=84984578929&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84984578929&partnerID=8YFLogxK

U2 - 10.1063/1.4936004

DO - 10.1063/1.4936004

M3 - Conference contribution

AN - SCOPUS:84984578929

VL - 1688

BT - New Operational Technologies, NEWOT 2015

A2 - Kistenev, Yury V.

A2 - Sharkeev, Yurii P.

A2 - Sadovoy, Mikhail A.

A2 - Orlov, Sergei N.

PB - American Institute of Physics Inc.

ER -