Plastic strain arrangement in copper single crystals in sliding

Andrey V. Chumaevskii, Sergei Yulievich Tarasov, Dmitry V. Lychagin

    Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

    1 цитирование (Scopus)

    Выдержка

    Deformation of tribologically loaded contact zone is one of the wear mechanisms in spite of the fact that no mass loss may occur during this process. Generation of optimal crystallographic orientations of the grains in a polycrystalline materials (texturing) may cause hardening and reducing the deformation wear. To reveal the orientation dependence of an individual gain and simplify the task we use copper single crystals with the orientations of the compression axis along [1 1 1] and [110]. The plastic deformation was investigated by means of optical, scanning electron microscopy and EBSD techniques. It was established that at least four different zones were generated in the course of sliding test, such as non-deformed base metal, plastic deformation layer sliding, crystalline lattice reorientation layer and subsurface grain structure layer. The maximum plastic strain penetration depth was observed on [110]-single crystals. The minimum stability of [1 1 1] -crystals with respect to rotation deformation mode as well as activation of shear in the sliding contact plane provide for rotation deformation localization below the worn surface. The high-rate accumulation of misorientations and less strain penetration depth was observed on [1 1 1] -crystals as compared to those of [110]-oriented ones.

    Язык оригиналаАнглийский
    Название основной публикацииAIP Conference Proceedings
    ИздательAmerican Institute of Physics Inc.
    Страницы91-94
    Число страниц4
    Том1623
    ISBN (печатное издание)9780735412606
    DOI
    СостояниеОпубликовано - 2014
    СобытиеInternational Conference on Physical Mesomechanics of Multilevel Systems 2014 - Tomsk, Российская Федерация
    Продолжительность: 3 сен 20145 сен 2014

    Другое

    ДругоеInternational Conference on Physical Mesomechanics of Multilevel Systems 2014
    СтранаРоссийская Федерация
    ГородTomsk
    Период3.9.145.9.14

    Отпечаток

    sliding
    plastics
    copper
    single crystals
    plastic deformation
    penetration
    sliding contact
    misalignment
    hardening
    retraining
    crystals
    activation
    shear
    scanning electron microscopy
    causes
    metals

    ASJC Scopus subject areas

    • Physics and Astronomy(all)

    Цитировать

    Chumaevskii, A. V., Tarasov, SY., & Lychagin, D. V. (2014). Plastic strain arrangement in copper single crystals in sliding. В AIP Conference Proceedings (Том 1623, стр. 91-94). American Institute of Physics Inc.. https://doi.org/10.1063/1.4898890

    Plastic strain arrangement in copper single crystals in sliding. / Chumaevskii, Andrey V.; Tarasov, Sergei Yulievich; Lychagin, Dmitry V.

    AIP Conference Proceedings. Том 1623 American Institute of Physics Inc., 2014. стр. 91-94.

    Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

    Chumaevskii, AV, Tarasov, SY & Lychagin, DV 2014, Plastic strain arrangement in copper single crystals in sliding. в AIP Conference Proceedings. том. 1623, American Institute of Physics Inc., стр. 91-94, International Conference on Physical Mesomechanics of Multilevel Systems 2014, Tomsk, Российская Федерация, 3.9.14. https://doi.org/10.1063/1.4898890
    Chumaevskii AV, Tarasov SY, Lychagin DV. Plastic strain arrangement in copper single crystals in sliding. В AIP Conference Proceedings. Том 1623. American Institute of Physics Inc. 2014. стр. 91-94 https://doi.org/10.1063/1.4898890
    Chumaevskii, Andrey V. ; Tarasov, Sergei Yulievich ; Lychagin, Dmitry V. / Plastic strain arrangement in copper single crystals in sliding. AIP Conference Proceedings. Том 1623 American Institute of Physics Inc., 2014. стр. 91-94
    @inproceedings{3165c8220620461d812039dcb5bbd7a5,
    title = "Plastic strain arrangement in copper single crystals in sliding",
    abstract = "Deformation of tribologically loaded contact zone is one of the wear mechanisms in spite of the fact that no mass loss may occur during this process. Generation of optimal crystallographic orientations of the grains in a polycrystalline materials (texturing) may cause hardening and reducing the deformation wear. To reveal the orientation dependence of an individual gain and simplify the task we use copper single crystals with the orientations of the compression axis along [1 1 1] and [110]. The plastic deformation was investigated by means of optical, scanning electron microscopy and EBSD techniques. It was established that at least four different zones were generated in the course of sliding test, such as non-deformed base metal, plastic deformation layer sliding, crystalline lattice reorientation layer and subsurface grain structure layer. The maximum plastic strain penetration depth was observed on [110]-single crystals. The minimum stability of [1 1 1] -crystals with respect to rotation deformation mode as well as activation of shear in the sliding contact plane provide for rotation deformation localization below the worn surface. The high-rate accumulation of misorientations and less strain penetration depth was observed on [1 1 1] -crystals as compared to those of [110]-oriented ones.",
    keywords = "Copper, EBSD, Fragmentation, Friction, Single crystal, Sliding",
    author = "Chumaevskii, {Andrey V.} and Sergei Yulievich Tarasov and Lychagin, {Dmitry V.}",
    year = "2014",
    doi = "10.1063/1.4898890",
    language = "English",
    isbn = "9780735412606",
    volume = "1623",
    pages = "91--94",
    booktitle = "AIP Conference Proceedings",
    publisher = "American Institute of Physics Inc.",

    }

    TY - GEN

    T1 - Plastic strain arrangement in copper single crystals in sliding

    AU - Chumaevskii, Andrey V.

    AU - Tarasov, Sergei Yulievich

    AU - Lychagin, Dmitry V.

    PY - 2014

    Y1 - 2014

    N2 - Deformation of tribologically loaded contact zone is one of the wear mechanisms in spite of the fact that no mass loss may occur during this process. Generation of optimal crystallographic orientations of the grains in a polycrystalline materials (texturing) may cause hardening and reducing the deformation wear. To reveal the orientation dependence of an individual gain and simplify the task we use copper single crystals with the orientations of the compression axis along [1 1 1] and [110]. The plastic deformation was investigated by means of optical, scanning electron microscopy and EBSD techniques. It was established that at least four different zones were generated in the course of sliding test, such as non-deformed base metal, plastic deformation layer sliding, crystalline lattice reorientation layer and subsurface grain structure layer. The maximum plastic strain penetration depth was observed on [110]-single crystals. The minimum stability of [1 1 1] -crystals with respect to rotation deformation mode as well as activation of shear in the sliding contact plane provide for rotation deformation localization below the worn surface. The high-rate accumulation of misorientations and less strain penetration depth was observed on [1 1 1] -crystals as compared to those of [110]-oriented ones.

    AB - Deformation of tribologically loaded contact zone is one of the wear mechanisms in spite of the fact that no mass loss may occur during this process. Generation of optimal crystallographic orientations of the grains in a polycrystalline materials (texturing) may cause hardening and reducing the deformation wear. To reveal the orientation dependence of an individual gain and simplify the task we use copper single crystals with the orientations of the compression axis along [1 1 1] and [110]. The plastic deformation was investigated by means of optical, scanning electron microscopy and EBSD techniques. It was established that at least four different zones were generated in the course of sliding test, such as non-deformed base metal, plastic deformation layer sliding, crystalline lattice reorientation layer and subsurface grain structure layer. The maximum plastic strain penetration depth was observed on [110]-single crystals. The minimum stability of [1 1 1] -crystals with respect to rotation deformation mode as well as activation of shear in the sliding contact plane provide for rotation deformation localization below the worn surface. The high-rate accumulation of misorientations and less strain penetration depth was observed on [1 1 1] -crystals as compared to those of [110]-oriented ones.

    KW - Copper

    KW - EBSD

    KW - Fragmentation

    KW - Friction

    KW - Single crystal

    KW - Sliding

    UR - http://www.scopus.com/inward/record.url?scp=84915789275&partnerID=8YFLogxK

    UR - http://www.scopus.com/inward/citedby.url?scp=84915789275&partnerID=8YFLogxK

    U2 - 10.1063/1.4898890

    DO - 10.1063/1.4898890

    M3 - Conference contribution

    AN - SCOPUS:84915789275

    SN - 9780735412606

    VL - 1623

    SP - 91

    EP - 94

    BT - AIP Conference Proceedings

    PB - American Institute of Physics Inc.

    ER -