Physico-chemical state of surface layers and exploitation properties of VT18U alloy irradiated by high power ion beam

A. N. Didenko, V. A. Shulov, G. E. Remnev, A. E. Strygin, A. D. Pogrebnyak, N. A. Nochovnaya, Yu D. Yagodkin

Результат исследований: Материалы для журналаСтатьярецензирование

6 Цитирования (Scopus)

Аннотация

Studies of chemico-physical and structural phase state of VT18U alloy surface layers under high-power ion beam of 20-160 A÷cm2 current density, diffusion vacuum annealing and post exploiting tests of fatigue limit, heat and dust errosion resistance were performed. Ion-beam treatment of the surface layer is shown to increase the impurity contents in surface layer and, as a result, to change the structural state, oxygen and aluminium concentration. The carbide formation has been observed. Optimal irradiation conditions (140-150 A÷cm2) cause the improvement of alloy exploitation characteristics. The fatigue limit increases by 10 %, cyclic endurance under 500° C and 370 MPa by 20 times, heat resistance under 550° C by 2.3 times and dust errosion resistance by 1.8 times.

Язык оригиналаАнглийский
Страницы (с-по)14-23
Число страниц10
ЖурналFizika i Khimiya Obrabotki Materialov
Номер выпуска5
СостояниеОпубликовано - сен 1991

ASJC Scopus subject areas

  • Materials Science(all)

Fingerprint Подробные сведения о темах исследования «Physico-chemical state of surface layers and exploitation properties of VT18U alloy irradiated by high power ion beam». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать