Phase composition and defect substructure of the zirconia nanopowder modified by the powerful ultrasonic assistance

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

Аннотация

Commercial nanopowder of the partially yttrium-stabilized zirconia (ZrO2+3 mol.% Y2O3) was treated by the non-cavitational powerful ultrasonic assistance (PUA). Influence of PUA on the microstructure and phase composition of the powder has been investigated by scanning and transmission electron microscopy. Investigated powder before and after PUA has polycrystalline structure. It was found that TZ-3YS particles after PUA have tetragonal and cubic zirconia phases; some of the particles consist of a mixture of monoclinic, tetragonal and cubic phases, but these particles have substructure with slight disorientation of crystallite fragments.

Язык оригиналаАнглийский
Название основной публикацииAdvanced Materials Research
Страницы180-183
Число страниц4
Том872
DOI
СостояниеОпубликовано - 2014
СобытиеRussian-German Forum on Nanotechnology - Tomsk, Российская Федерация
Продолжительность: 21 мая 201324 мая 2013

Серия публикаций

НазваниеAdvanced Materials Research
Том872
ISSN (печатное издание)10226680

Другое

ДругоеRussian-German Forum on Nanotechnology
СтранаРоссийская Федерация
ГородTomsk
Период21.5.1324.5.13

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint Подробные сведения о темах исследования «Phase composition and defect substructure of the zirconia nanopowder modified by the powerful ultrasonic assistance». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать