Modification of hypereutectic silumin by ion-electron-plasma method

Maria E. Rygina, Yurii F. Ivanov, Alexander P. Laskovnev, Anton D. Teresov, Nikolay N. Cherenda, Vladimir V. Uglov, Elizaveta A. Petrikova, Olga V. Krysina

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

Выдержка

Hypereutectic silumin is aluminum-silicon alloy. It is widely used as the material for producing pistons and sliding bearings. The samples were obtained in Belorussian State University and in the Physical-Technical Institute of the National Academy of Sciences. The percentage of silicon is 18-20 wt.%. The structure has a large number of pores and cracks. The size of pores is 100 μm. The method of modification have been carried out in two steps. The first step is ion-plasma deposition ZrTiCu coating. The second step is melting the coating into the substrate. After modification microhardness is 3.2 GPa, wear resistance is 1.8 times less than in the untreated samples. The crystallites size is 0.2-0.4 μm. Thus, this method allows obtaining alloys in the near-surface layer, grinding the structure and increasing mechanical characteristics.

Язык оригиналаАнглийский
Название основной публикацииHigh Technology
Подзаголовок основной публикацииResearch and Applications 2017
РедакторыGeorgii E. Osokin, Ekaterina A. Kulinich
ИздательTrans Tech Publications Ltd
Страницы54-59
Число страниц6
ISBN (печатное издание)9783035712810
DOI
СостояниеОпубликовано - 1 янв 2018
Событие6th International Conference for Young Scientists High Technology: Research and Applications, HTRA 2017 - Tomsk, Российская Федерация
Продолжительность: 27 ноя 201729 ноя 2017

Серия публикаций

НазваниеKey Engineering Materials
Том769 KEM
ISSN (печатное издание)1013-9826

Конференция

Конференция6th International Conference for Young Scientists High Technology: Research and Applications, HTRA 2017
СтранаРоссийская Федерация
ГородTomsk
Период27.11.1729.11.17

Отпечаток

Bearings (structural)
Ions
Plasmas
Plasma deposition
Coatings
Silicon alloys
Electrons
Silicon
Crystallites
Pistons
Microhardness
Wear resistance
Aluminum alloys
Melting
Cracks
Substrates

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Цитировать

Rygina, M. E., Ivanov, Y. F., Laskovnev, A. P., Teresov, A. D., Cherenda, N. N., Uglov, V. V., ... Krysina, O. V. (2018). Modification of hypereutectic silumin by ion-electron-plasma method. В G. E. Osokin, & E. A. Kulinich (Ред.), High Technology: Research and Applications 2017 (стр. 54-59). (Key Engineering Materials; Том 769 KEM). Trans Tech Publications Ltd. https://doi.org/10.4028/www.scientific.net/KEM.769.54

Modification of hypereutectic silumin by ion-electron-plasma method. / Rygina, Maria E.; Ivanov, Yurii F.; Laskovnev, Alexander P.; Teresov, Anton D.; Cherenda, Nikolay N.; Uglov, Vladimir V.; Petrikova, Elizaveta A.; Krysina, Olga V.

High Technology: Research and Applications 2017. ред. / Georgii E. Osokin; Ekaterina A. Kulinich. Trans Tech Publications Ltd, 2018. стр. 54-59 (Key Engineering Materials; Том 769 KEM).

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

Rygina, ME, Ivanov, YF, Laskovnev, AP, Teresov, AD, Cherenda, NN, Uglov, VV, Petrikova, EA & Krysina, OV 2018, Modification of hypereutectic silumin by ion-electron-plasma method. в GE Osokin & EA Kulinich (ред.), High Technology: Research and Applications 2017. Key Engineering Materials, том. 769 KEM, Trans Tech Publications Ltd, стр. 54-59, 6th International Conference for Young Scientists High Technology: Research and Applications, HTRA 2017, Tomsk, Российская Федерация, 27.11.17. https://doi.org/10.4028/www.scientific.net/KEM.769.54
Rygina ME, Ivanov YF, Laskovnev AP, Teresov AD, Cherenda NN, Uglov VV и соавт. Modification of hypereutectic silumin by ion-electron-plasma method. В Osokin GE, Kulinich EA, редакторы, High Technology: Research and Applications 2017. Trans Tech Publications Ltd. 2018. стр. 54-59. (Key Engineering Materials). https://doi.org/10.4028/www.scientific.net/KEM.769.54
Rygina, Maria E. ; Ivanov, Yurii F. ; Laskovnev, Alexander P. ; Teresov, Anton D. ; Cherenda, Nikolay N. ; Uglov, Vladimir V. ; Petrikova, Elizaveta A. ; Krysina, Olga V. / Modification of hypereutectic silumin by ion-electron-plasma method. High Technology: Research and Applications 2017. редактор / Georgii E. Osokin ; Ekaterina A. Kulinich. Trans Tech Publications Ltd, 2018. стр. 54-59 (Key Engineering Materials).
@inproceedings{42c1421a56514938a0579993e23aca69,
title = "Modification of hypereutectic silumin by ion-electron-plasma method",
abstract = "Hypereutectic silumin is aluminum-silicon alloy. It is widely used as the material for producing pistons and sliding bearings. The samples were obtained in Belorussian State University and in the Physical-Technical Institute of the National Academy of Sciences. The percentage of silicon is 18-20 wt.{\%}. The structure has a large number of pores and cracks. The size of pores is 100 μm. The method of modification have been carried out in two steps. The first step is ion-plasma deposition ZrTiCu coating. The second step is melting the coating into the substrate. After modification microhardness is 3.2 GPa, wear resistance is 1.8 times less than in the untreated samples. The crystallites size is 0.2-0.4 μm. Thus, this method allows obtaining alloys in the near-surface layer, grinding the structure and increasing mechanical characteristics.",
keywords = "Defects, Electron beam, Film / substrate system, Hardness, Hypereutectic silumin, Ion-plasma coating, Silumin",
author = "Rygina, {Maria E.} and Ivanov, {Yurii F.} and Laskovnev, {Alexander P.} and Teresov, {Anton D.} and Cherenda, {Nikolay N.} and Uglov, {Vladimir V.} and Petrikova, {Elizaveta A.} and Krysina, {Olga V.}",
year = "2018",
month = "1",
day = "1",
doi = "10.4028/www.scientific.net/KEM.769.54",
language = "English",
isbn = "9783035712810",
series = "Key Engineering Materials",
publisher = "Trans Tech Publications Ltd",
pages = "54--59",
editor = "Osokin, {Georgii E.} and Kulinich, {Ekaterina A.}",
booktitle = "High Technology",

}

TY - GEN

T1 - Modification of hypereutectic silumin by ion-electron-plasma method

AU - Rygina, Maria E.

AU - Ivanov, Yurii F.

AU - Laskovnev, Alexander P.

AU - Teresov, Anton D.

AU - Cherenda, Nikolay N.

AU - Uglov, Vladimir V.

AU - Petrikova, Elizaveta A.

AU - Krysina, Olga V.

PY - 2018/1/1

Y1 - 2018/1/1

N2 - Hypereutectic silumin is aluminum-silicon alloy. It is widely used as the material for producing pistons and sliding bearings. The samples were obtained in Belorussian State University and in the Physical-Technical Institute of the National Academy of Sciences. The percentage of silicon is 18-20 wt.%. The structure has a large number of pores and cracks. The size of pores is 100 μm. The method of modification have been carried out in two steps. The first step is ion-plasma deposition ZrTiCu coating. The second step is melting the coating into the substrate. After modification microhardness is 3.2 GPa, wear resistance is 1.8 times less than in the untreated samples. The crystallites size is 0.2-0.4 μm. Thus, this method allows obtaining alloys in the near-surface layer, grinding the structure and increasing mechanical characteristics.

AB - Hypereutectic silumin is aluminum-silicon alloy. It is widely used as the material for producing pistons and sliding bearings. The samples were obtained in Belorussian State University and in the Physical-Technical Institute of the National Academy of Sciences. The percentage of silicon is 18-20 wt.%. The structure has a large number of pores and cracks. The size of pores is 100 μm. The method of modification have been carried out in two steps. The first step is ion-plasma deposition ZrTiCu coating. The second step is melting the coating into the substrate. After modification microhardness is 3.2 GPa, wear resistance is 1.8 times less than in the untreated samples. The crystallites size is 0.2-0.4 μm. Thus, this method allows obtaining alloys in the near-surface layer, grinding the structure and increasing mechanical characteristics.

KW - Defects

KW - Electron beam

KW - Film / substrate system

KW - Hardness

KW - Hypereutectic silumin

KW - Ion-plasma coating

KW - Silumin

UR - http://www.scopus.com/inward/record.url?scp=85046420388&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85046420388&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/KEM.769.54

DO - 10.4028/www.scientific.net/KEM.769.54

M3 - Conference contribution

AN - SCOPUS:85046420388

SN - 9783035712810

T3 - Key Engineering Materials

SP - 54

EP - 59

BT - High Technology

A2 - Osokin, Georgii E.

A2 - Kulinich, Ekaterina A.

PB - Trans Tech Publications Ltd

ER -