Modification of hard alloy by the action of high power ion beams

Vladimir Vasilevich Uglov, G. E. Remnev, A. K. Kuleshov, M. S. Saltymakov

Результат исследований: Материалы для журналаСтатьярецензирование

11 Цитирования (Scopus)


Phase composition, sizes of coherent scattering regions, hardness and friction coefficient of WC-TiC-Co hard alloy and "(Ti,Cr)N coating-on-alloy" system treated by high power ion beams (HPIB) are studied. HPIB treatment was carried out with power densities from 4 to 16J/cm2. The effect of HPIB pretreatment (4J/cm2) before deposition procedure was studied. HPIB action with energy densities of 8-16J/cm2 on hard alloy results in partial fusion of tungsten and titanium carbides. The hardness of surface layer increases by two times and wear resistance improves. HPIB action on "coating-on-alloy" system leads to coarsening of (Ti,Cr)N crystallites, partial decomposition of (Ti,Cr)N and precipitation of chromium phase. Preliminary HPIB treatment (4J/cm2) followed by HPIB impact (16J/cm2) provides best effect on wear-resistance of (Ti,Cr)N solid solution on hard alloy.

Язык оригиналаАнглийский
Страницы (с-по)781-784
Число страниц4
ЖурналSurface and Coatings Technology
Номер выпуска5
СостояниеОпубликовано - 25 ноя 2011

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry
  • Surfaces, Coatings and Films
  • Surfaces and Interfaces

Fingerprint Подробные сведения о темах исследования «Modification of hard alloy by the action of high power ion beams». Вместе они формируют уникальный семантический отпечаток (fingerprint).