Microstructure stability and mechanical properties of ultrafine-grained zirconium alloy under prolonged thermal exposure

Yury Petrovich Sharkeev, Anna Yu Eroshenko, Pavel V. Uvarkin, Alexey I. Tolmachev, Nesibeli K. Akhmetova

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

Выдержка

The paper describes the experimental results in microstructure thermal stability and mechanical properties of ultrafine-grained zirconium alloy with 1 mass % Nb (Zr-1 mass %Nb) under prolonged thermal exposure. Ultrafine-grained zirconium alloy is produced by severe plastic deformation (SPD) method. It was proved that SPD method including multiple abc-pressing and multi-pass rolling, as well as further pre-recrystallizing annealing enhances the formation of ultrafine-grained structures with mean element size of 0.2 μm. Thermostability time interval of ultrafine-grained structure and the mechanical properties (in case of microhardness) under prolonged thermal exposure (up to 360 hours) for zirconium alloy was experimentally determined. It was proved that ultrafine-grained structure is stable at 400°? within 10 hours whilst keeping the microhardness level attained after SPD. In cases of continuous annealing time from 24 to 360 hours recrystallization processes develop intensively, followed by the decrease in microhardness and intensive growth of structure elements within the alloy.

Язык оригиналаАнглийский
Название основной публикацииAdvanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016: Proceedings of the International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016
ИздательAmerican Institute of Physics Inc.
Том1783
ISBN (электронное издание)9780735414457
DOI
СостояниеОпубликовано - 10 ноя 2016
СобытиеInternational Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016 - Tomsk, Российская Федерация
Продолжительность: 19 сен 201623 сен 2016

Конференция

КонференцияInternational Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016
СтранаРоссийская Федерация
ГородTomsk
Период19.9.1623.9.16

Отпечаток

zirconium alloys
microhardness
plastic deformation
mechanical properties
microstructure
thermal stability
annealing
pressing
intervals

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Цитировать

Sharkeev, Y. P., Eroshenko, A. Y., Uvarkin, P. V., Tolmachev, A. I., & Akhmetova, N. K. (2016). Microstructure stability and mechanical properties of ultrafine-grained zirconium alloy under prolonged thermal exposure. В Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016: Proceedings of the International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016 (Том 1783). [020205] American Institute of Physics Inc.. https://doi.org/10.1063/1.4966499

Microstructure stability and mechanical properties of ultrafine-grained zirconium alloy under prolonged thermal exposure. / Sharkeev, Yury Petrovich; Eroshenko, Anna Yu; Uvarkin, Pavel V.; Tolmachev, Alexey I.; Akhmetova, Nesibeli K.

Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016: Proceedings of the International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016. Том 1783 American Institute of Physics Inc., 2016. 020205.

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

Sharkeev, YP, Eroshenko, AY, Uvarkin, PV, Tolmachev, AI & Akhmetova, NK 2016, Microstructure stability and mechanical properties of ultrafine-grained zirconium alloy under prolonged thermal exposure. в Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016: Proceedings of the International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016. том. 1783, 020205, American Institute of Physics Inc., Tomsk, Российская Федерация, 19.9.16. https://doi.org/10.1063/1.4966499
Sharkeev YP, Eroshenko AY, Uvarkin PV, Tolmachev AI, Akhmetova NK. Microstructure stability and mechanical properties of ultrafine-grained zirconium alloy under prolonged thermal exposure. В Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016: Proceedings of the International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016. Том 1783. American Institute of Physics Inc. 2016. 020205 https://doi.org/10.1063/1.4966499
Sharkeev, Yury Petrovich ; Eroshenko, Anna Yu ; Uvarkin, Pavel V. ; Tolmachev, Alexey I. ; Akhmetova, Nesibeli K. / Microstructure stability and mechanical properties of ultrafine-grained zirconium alloy under prolonged thermal exposure. Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016: Proceedings of the International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016. Том 1783 American Institute of Physics Inc., 2016.
@inproceedings{74089733cc774659b71a28a9f3245e29,
title = "Microstructure stability and mechanical properties of ultrafine-grained zirconium alloy under prolonged thermal exposure",
abstract = "The paper describes the experimental results in microstructure thermal stability and mechanical properties of ultrafine-grained zirconium alloy with 1 mass {\%} Nb (Zr-1 mass {\%}Nb) under prolonged thermal exposure. Ultrafine-grained zirconium alloy is produced by severe plastic deformation (SPD) method. It was proved that SPD method including multiple abc-pressing and multi-pass rolling, as well as further pre-recrystallizing annealing enhances the formation of ultrafine-grained structures with mean element size of 0.2 μm. Thermostability time interval of ultrafine-grained structure and the mechanical properties (in case of microhardness) under prolonged thermal exposure (up to 360 hours) for zirconium alloy was experimentally determined. It was proved that ultrafine-grained structure is stable at 400°? within 10 hours whilst keeping the microhardness level attained after SPD. In cases of continuous annealing time from 24 to 360 hours recrystallization processes develop intensively, followed by the decrease in microhardness and intensive growth of structure elements within the alloy.",
author = "Sharkeev, {Yury Petrovich} and Eroshenko, {Anna Yu} and Uvarkin, {Pavel V.} and Tolmachev, {Alexey I.} and Akhmetova, {Nesibeli K.}",
year = "2016",
month = "11",
day = "10",
doi = "10.1063/1.4966499",
language = "English",
volume = "1783",
booktitle = "Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016: Proceedings of the International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016",
publisher = "American Institute of Physics Inc.",

}

TY - GEN

T1 - Microstructure stability and mechanical properties of ultrafine-grained zirconium alloy under prolonged thermal exposure

AU - Sharkeev, Yury Petrovich

AU - Eroshenko, Anna Yu

AU - Uvarkin, Pavel V.

AU - Tolmachev, Alexey I.

AU - Akhmetova, Nesibeli K.

PY - 2016/11/10

Y1 - 2016/11/10

N2 - The paper describes the experimental results in microstructure thermal stability and mechanical properties of ultrafine-grained zirconium alloy with 1 mass % Nb (Zr-1 mass %Nb) under prolonged thermal exposure. Ultrafine-grained zirconium alloy is produced by severe plastic deformation (SPD) method. It was proved that SPD method including multiple abc-pressing and multi-pass rolling, as well as further pre-recrystallizing annealing enhances the formation of ultrafine-grained structures with mean element size of 0.2 μm. Thermostability time interval of ultrafine-grained structure and the mechanical properties (in case of microhardness) under prolonged thermal exposure (up to 360 hours) for zirconium alloy was experimentally determined. It was proved that ultrafine-grained structure is stable at 400°? within 10 hours whilst keeping the microhardness level attained after SPD. In cases of continuous annealing time from 24 to 360 hours recrystallization processes develop intensively, followed by the decrease in microhardness and intensive growth of structure elements within the alloy.

AB - The paper describes the experimental results in microstructure thermal stability and mechanical properties of ultrafine-grained zirconium alloy with 1 mass % Nb (Zr-1 mass %Nb) under prolonged thermal exposure. Ultrafine-grained zirconium alloy is produced by severe plastic deformation (SPD) method. It was proved that SPD method including multiple abc-pressing and multi-pass rolling, as well as further pre-recrystallizing annealing enhances the formation of ultrafine-grained structures with mean element size of 0.2 μm. Thermostability time interval of ultrafine-grained structure and the mechanical properties (in case of microhardness) under prolonged thermal exposure (up to 360 hours) for zirconium alloy was experimentally determined. It was proved that ultrafine-grained structure is stable at 400°? within 10 hours whilst keeping the microhardness level attained after SPD. In cases of continuous annealing time from 24 to 360 hours recrystallization processes develop intensively, followed by the decrease in microhardness and intensive growth of structure elements within the alloy.

UR - http://www.scopus.com/inward/record.url?scp=85006010831&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85006010831&partnerID=8YFLogxK

U2 - 10.1063/1.4966499

DO - 10.1063/1.4966499

M3 - Conference contribution

AN - SCOPUS:85006010831

VL - 1783

BT - Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016: Proceedings of the International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016

PB - American Institute of Physics Inc.

ER -