Magnetic silica hybrids modified with guanidine containing co-polymers for drug delivery applications

Alexander S. Timin, Svetlana Yu Khashirova, Evgeniy V. Rumyantsev, Alexander A. Goncharenko

Результат исследований: Материалы для журналаСтатья

14 Цитирования (Scopus)

Выдержка

Guanidine containing co-polymers grafted onto silica nanoparticles to form core-shell structure were prepared by sol-gel method in the presence of γ-Fe2O3 nanoparticles. The morphological features for uncoated and coated silica particles have been characterized with scanning electron microscopy. The results show that the polymer coated silicas exhibit spherical morphology with rough polymeric surface covered by γ-Fe2O3 nanoparticles. The grafting amount of guanidine containing co-polymers evaluated by thermogravimetric analysis was in the range from 17 to 30%. Then, the drug loading properties and cumulative release of silica hybrids modified with guanidine containing co-polymers were evaluated using molsidomine as a model drug. It was shown that after polymer grafting the loading content of molsidomine could reach up to 3.42 ± 0.21 and 2.34 ± 0.14 mg/g respectively. The maximum drug release of molsidomine is achieved at pH 1.6 (approximately 71-75% release at 37 °C), whereas at pH 7.4 drug release is lower (50.4-59.6% release at 37 °C). These results have an important implication that our magneto-controlled silica hybrids modified with guanidine containing co-polymers are promising as drug carriers with controlled behaviour under influence of magnetic field.

Язык оригиналаАнглийский
Страницы (с-по)20-28
Число страниц9
ЖурналMaterials Science and Engineering C
Том64
DOI
СостояниеОпубликовано - 1 июл 2016

Отпечаток

guanidines
Guanidine
Drug delivery
Silicon Dioxide
delivery
Polymers
drugs
Molsidomine
Silica
silicon dioxide
polymers
Nanoparticles
Pharmaceutical Preparations
nanoparticles
Drug Carriers
Sol-gel process
Thermogravimetric analysis
gels
Magnetic fields
Scanning electron microscopy

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanical Engineering
  • Mechanics of Materials

Цитировать

Magnetic silica hybrids modified with guanidine containing co-polymers for drug delivery applications. / Timin, Alexander S.; Khashirova, Svetlana Yu; Rumyantsev, Evgeniy V.; Goncharenko, Alexander A.

В: Materials Science and Engineering C, Том 64, 01.07.2016, стр. 20-28.

Результат исследований: Материалы для журналаСтатья

Timin, Alexander S. ; Khashirova, Svetlana Yu ; Rumyantsev, Evgeniy V. ; Goncharenko, Alexander A. / Magnetic silica hybrids modified with guanidine containing co-polymers for drug delivery applications. В: Materials Science and Engineering C. 2016 ; Том 64. стр. 20-28.
@article{3721184958384867bd0ccea6832b6675,
title = "Magnetic silica hybrids modified with guanidine containing co-polymers for drug delivery applications",
abstract = "Guanidine containing co-polymers grafted onto silica nanoparticles to form core-shell structure were prepared by sol-gel method in the presence of γ-Fe2O3 nanoparticles. The morphological features for uncoated and coated silica particles have been characterized with scanning electron microscopy. The results show that the polymer coated silicas exhibit spherical morphology with rough polymeric surface covered by γ-Fe2O3 nanoparticles. The grafting amount of guanidine containing co-polymers evaluated by thermogravimetric analysis was in the range from 17 to 30{\%}. Then, the drug loading properties and cumulative release of silica hybrids modified with guanidine containing co-polymers were evaluated using molsidomine as a model drug. It was shown that after polymer grafting the loading content of molsidomine could reach up to 3.42 ± 0.21 and 2.34 ± 0.14 mg/g respectively. The maximum drug release of molsidomine is achieved at pH 1.6 (approximately 71-75{\%} release at 37 °C), whereas at pH 7.4 drug release is lower (50.4-59.6{\%} release at 37 °C). These results have an important implication that our magneto-controlled silica hybrids modified with guanidine containing co-polymers are promising as drug carriers with controlled behaviour under influence of magnetic field.",
keywords = "Core-shell structure, Drug carrier, Magnetic properties, Polymer grafting, Silica core",
author = "Timin, {Alexander S.} and Khashirova, {Svetlana Yu} and Rumyantsev, {Evgeniy V.} and Goncharenko, {Alexander A.}",
year = "2016",
month = "7",
day = "1",
doi = "10.1016/j.msec.2016.03.057",
language = "English",
volume = "64",
pages = "20--28",
journal = "Materials Science and Engineering C",
issn = "0928-4931",
publisher = "Elsevier BV",

}

TY - JOUR

T1 - Magnetic silica hybrids modified with guanidine containing co-polymers for drug delivery applications

AU - Timin, Alexander S.

AU - Khashirova, Svetlana Yu

AU - Rumyantsev, Evgeniy V.

AU - Goncharenko, Alexander A.

PY - 2016/7/1

Y1 - 2016/7/1

N2 - Guanidine containing co-polymers grafted onto silica nanoparticles to form core-shell structure were prepared by sol-gel method in the presence of γ-Fe2O3 nanoparticles. The morphological features for uncoated and coated silica particles have been characterized with scanning electron microscopy. The results show that the polymer coated silicas exhibit spherical morphology with rough polymeric surface covered by γ-Fe2O3 nanoparticles. The grafting amount of guanidine containing co-polymers evaluated by thermogravimetric analysis was in the range from 17 to 30%. Then, the drug loading properties and cumulative release of silica hybrids modified with guanidine containing co-polymers were evaluated using molsidomine as a model drug. It was shown that after polymer grafting the loading content of molsidomine could reach up to 3.42 ± 0.21 and 2.34 ± 0.14 mg/g respectively. The maximum drug release of molsidomine is achieved at pH 1.6 (approximately 71-75% release at 37 °C), whereas at pH 7.4 drug release is lower (50.4-59.6% release at 37 °C). These results have an important implication that our magneto-controlled silica hybrids modified with guanidine containing co-polymers are promising as drug carriers with controlled behaviour under influence of magnetic field.

AB - Guanidine containing co-polymers grafted onto silica nanoparticles to form core-shell structure were prepared by sol-gel method in the presence of γ-Fe2O3 nanoparticles. The morphological features for uncoated and coated silica particles have been characterized with scanning electron microscopy. The results show that the polymer coated silicas exhibit spherical morphology with rough polymeric surface covered by γ-Fe2O3 nanoparticles. The grafting amount of guanidine containing co-polymers evaluated by thermogravimetric analysis was in the range from 17 to 30%. Then, the drug loading properties and cumulative release of silica hybrids modified with guanidine containing co-polymers were evaluated using molsidomine as a model drug. It was shown that after polymer grafting the loading content of molsidomine could reach up to 3.42 ± 0.21 and 2.34 ± 0.14 mg/g respectively. The maximum drug release of molsidomine is achieved at pH 1.6 (approximately 71-75% release at 37 °C), whereas at pH 7.4 drug release is lower (50.4-59.6% release at 37 °C). These results have an important implication that our magneto-controlled silica hybrids modified with guanidine containing co-polymers are promising as drug carriers with controlled behaviour under influence of magnetic field.

KW - Core-shell structure

KW - Drug carrier

KW - Magnetic properties

KW - Polymer grafting

KW - Silica core

UR - http://www.scopus.com/inward/record.url?scp=84961644791&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84961644791&partnerID=8YFLogxK

U2 - 10.1016/j.msec.2016.03.057

DO - 10.1016/j.msec.2016.03.057

M3 - Article

AN - SCOPUS:84961644791

VL - 64

SP - 20

EP - 28

JO - Materials Science and Engineering C

JF - Materials Science and Engineering C

SN - 0928-4931

ER -