Low temperature synthesis of composition poros materials from mortar sands

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

Аннотация

It is established that the eliminations of construction sand with the content of SiO<inf>2</inf> about 70 wt. % and particle size less than 60 μm are suitable for the production of a foamglass-crystal material on the basis of the low-temperature frit, which was synthesized at the temperature 900°C. The obtained foamglass-crystal material exceeds foamglass (by 3.0 times) and clayite (by 1.5 times) by strength and is characterized by low value of water absorption (0.1 %).

Язык оригиналаАнглийский
Название основной публикацииIOP Conference Series: Materials Science and Engineering
Том64
Издание1
DOI
СостояниеОпубликовано - 2014
Событие2nd International Conference on Structural Nano Composites, NANOSTRUC 2014 - Madrid, Испания
Продолжительность: 20 мая 201421 мая 2014

Другое

Другое2nd International Conference on Structural Nano Composites, NANOSTRUC 2014
СтранаИспания
ГородMadrid
Период20.5.1421.5.14

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Fingerprint Подробные сведения о темах исследования «Low temperature synthesis of composition poros materials from mortar sands». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать

    Kazmina, O. V., Volland, S. N., & Dushkina, M. A. (2014). Low temperature synthesis of composition poros materials from mortar sands. В IOP Conference Series: Materials Science and Engineering (1 ред., Том 64). [012015] https://doi.org/10.1088/1757-899X/64/1/012015