In-situ X-ray diffraction studies of time and thickness dependence of crystallization of amorphous TiO2 thin films and stress evolution

R. Kužel, L. Nichtová, Z. Matěj, J. Musil

Результат исследований: Материалы для журналаСтатья

15 Цитирования (Scopus)

Выдержка

Remarkable properties of titanium dioxide films such as hydrophilicity or photocatalytic activity depend largely on their phase composition, microstructure and in particular on the crystallinity. By in-situ X-ray diffraction studies of isochronal and isothermal annealing of amorphous films with different thickness at different temperatures it was found that the crystallization process can be quite well described by the Johnson-Mehl-Avrami- Kolmogorov formula modified by the introduction of crystallization onset. This and other parameters of the formula strongly depend on the film thickness. For thickness below about 500 nm the crystallization is very slow. Simultaneously, the appearance and increase of tensile stresses with the annealing time were observed and these stresses were confirmed by detailed studies by both total pattern fitting and sin2ψ method on post-annealed samples. The stresses rapidly increase with decreasing thickness of the films. It seems that there is a strong correlation between the stresses and crystallization onset and/or crystallization rate. Tensile stresses that are generated during crystallization further inhibit crystallization and cause significant thickness dependence of the crystallization. The temperature and time dependence of microstructure of crystallized amorphous films differ significantly from those obtained for as-deposited nanocrystalline films or nanocrystalline powders. During annealing, quite large crystallites are formed quickly with the preferred orientation (001) that is suppressed with the proceeding time.

Язык оригиналаАнглийский
Страницы (с-по)1649-1654
Число страниц6
ЖурналThin Solid Films
Том519
Номер выпуска5
DOI
СостояниеОпубликовано - 30 дек 2010

Отпечаток

Amorphous films
Crystallization
time dependence
crystallization
X ray diffraction
Thin films
thin films
diffraction
x rays
tensile stress
Tensile stress
annealing
Annealing
Nanocrystalline powders
Isothermal annealing
microstructure
Microstructure
Hydrophilicity
Crystallites
Phase composition

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Metals and Alloys
  • Materials Chemistry

Цитировать

In-situ X-ray diffraction studies of time and thickness dependence of crystallization of amorphous TiO2 thin films and stress evolution. / Kužel, R.; Nichtová, L.; Matěj, Z.; Musil, J.

В: Thin Solid Films, Том 519, № 5, 30.12.2010, стр. 1649-1654.

Результат исследований: Материалы для журналаСтатья

@article{77e6f3756bc74f2487fa4e3c1e7402c8,
title = "In-situ X-ray diffraction studies of time and thickness dependence of crystallization of amorphous TiO2 thin films and stress evolution",
abstract = "Remarkable properties of titanium dioxide films such as hydrophilicity or photocatalytic activity depend largely on their phase composition, microstructure and in particular on the crystallinity. By in-situ X-ray diffraction studies of isochronal and isothermal annealing of amorphous films with different thickness at different temperatures it was found that the crystallization process can be quite well described by the Johnson-Mehl-Avrami- Kolmogorov formula modified by the introduction of crystallization onset. This and other parameters of the formula strongly depend on the film thickness. For thickness below about 500 nm the crystallization is very slow. Simultaneously, the appearance and increase of tensile stresses with the annealing time were observed and these stresses were confirmed by detailed studies by both total pattern fitting and sin2ψ method on post-annealed samples. The stresses rapidly increase with decreasing thickness of the films. It seems that there is a strong correlation between the stresses and crystallization onset and/or crystallization rate. Tensile stresses that are generated during crystallization further inhibit crystallization and cause significant thickness dependence of the crystallization. The temperature and time dependence of microstructure of crystallized amorphous films differ significantly from those obtained for as-deposited nanocrystalline films or nanocrystalline powders. During annealing, quite large crystallites are formed quickly with the preferred orientation (001) that is suppressed with the proceeding time.",
author = "R. Kužel and L. Nichtov{\'a} and Z. Matěj and J. Musil",
year = "2010",
month = "12",
day = "30",
doi = "10.1016/j.tsf.2010.08.122",
language = "English",
volume = "519",
pages = "1649--1654",
journal = "Thin Solid Films",
issn = "0040-6090",
publisher = "Elsevier",
number = "5",

}

TY - JOUR

T1 - In-situ X-ray diffraction studies of time and thickness dependence of crystallization of amorphous TiO2 thin films and stress evolution

AU - Kužel, R.

AU - Nichtová, L.

AU - Matěj, Z.

AU - Musil, J.

PY - 2010/12/30

Y1 - 2010/12/30

N2 - Remarkable properties of titanium dioxide films such as hydrophilicity or photocatalytic activity depend largely on their phase composition, microstructure and in particular on the crystallinity. By in-situ X-ray diffraction studies of isochronal and isothermal annealing of amorphous films with different thickness at different temperatures it was found that the crystallization process can be quite well described by the Johnson-Mehl-Avrami- Kolmogorov formula modified by the introduction of crystallization onset. This and other parameters of the formula strongly depend on the film thickness. For thickness below about 500 nm the crystallization is very slow. Simultaneously, the appearance and increase of tensile stresses with the annealing time were observed and these stresses were confirmed by detailed studies by both total pattern fitting and sin2ψ method on post-annealed samples. The stresses rapidly increase with decreasing thickness of the films. It seems that there is a strong correlation between the stresses and crystallization onset and/or crystallization rate. Tensile stresses that are generated during crystallization further inhibit crystallization and cause significant thickness dependence of the crystallization. The temperature and time dependence of microstructure of crystallized amorphous films differ significantly from those obtained for as-deposited nanocrystalline films or nanocrystalline powders. During annealing, quite large crystallites are formed quickly with the preferred orientation (001) that is suppressed with the proceeding time.

AB - Remarkable properties of titanium dioxide films such as hydrophilicity or photocatalytic activity depend largely on their phase composition, microstructure and in particular on the crystallinity. By in-situ X-ray diffraction studies of isochronal and isothermal annealing of amorphous films with different thickness at different temperatures it was found that the crystallization process can be quite well described by the Johnson-Mehl-Avrami- Kolmogorov formula modified by the introduction of crystallization onset. This and other parameters of the formula strongly depend on the film thickness. For thickness below about 500 nm the crystallization is very slow. Simultaneously, the appearance and increase of tensile stresses with the annealing time were observed and these stresses were confirmed by detailed studies by both total pattern fitting and sin2ψ method on post-annealed samples. The stresses rapidly increase with decreasing thickness of the films. It seems that there is a strong correlation between the stresses and crystallization onset and/or crystallization rate. Tensile stresses that are generated during crystallization further inhibit crystallization and cause significant thickness dependence of the crystallization. The temperature and time dependence of microstructure of crystallized amorphous films differ significantly from those obtained for as-deposited nanocrystalline films or nanocrystalline powders. During annealing, quite large crystallites are formed quickly with the preferred orientation (001) that is suppressed with the proceeding time.

UR - http://www.scopus.com/inward/record.url?scp=78649802776&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=78649802776&partnerID=8YFLogxK

U2 - 10.1016/j.tsf.2010.08.122

DO - 10.1016/j.tsf.2010.08.122

M3 - Article

AN - SCOPUS:78649802776

VL - 519

SP - 1649

EP - 1654

JO - Thin Solid Films

JF - Thin Solid Films

SN - 0040-6090

IS - 5

ER -