Impact toughness of 12Cr1MoV steel. Part 1 - Influence of temperature on energy and deformation parameters of fracture

Sergey V. Panin, P. O. Maruschak, I. V. Vlasov, B. B. Ovechkin

Результат исследований: Материалы для журналаСтатья

13 Цитирования (Scopus)

Аннотация

In the paper, the study of the impact toughness of 12Cr1MoV steel Charpy specimens at the temperature range from 20 °C to 600 °C is presented. It was revealed that the increase of the testing temperature from 20 °C to 375 °C and then to 600 °C causes the impact toughness to decrease by 1.2 and 2.42 times, respectively. The maximum energy of crack propagation during impact loading was observed at T = 375 °C, which is related to the increased resistance to crack propagation (cracking resistance) and sufficient strength (load capacity) of 12Cr1MoV steel. An approach to the quantitative description of impact fracture process was developed that includes the measurement of shear lip size as a quantitative fracture parameter. Scanning electron microscopy (SEM) was used to reveal and justify the reduction of load capacity at increased testing temperature and simultaneous increase of ductility and to describe the rival influence of such factors on the behavior and work of impact fracture.

Язык оригиналаАнглийский
Страницы (с-по)105-113
Число страниц9
ЖурналTheoretical and Applied Fracture Mechanics
Том83
DOI
СостояниеОпубликовано - 1 июн 2016

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanical Engineering
  • Applied Mathematics

Fingerprint Подробные сведения о темах исследования «Impact toughness of 12Cr1MoV steel. Part 1 - Influence of temperature on energy and deformation parameters of fracture». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать