Hybrid calcium phosphate coatings for implants

Результат исследований: Материалы для журналаСтатья

2 Цитирования (Scopus)

Аннотация

Monophasic biomaterials cannot provide all the necessary functions of bones or other calcined tissues. It is necessary to create for cancer patients the multiphase materials with the structure and composition simulating the natural bone. Such materials are classified as hybrid, obtained by a combination of chemically different components. The paper presents the physical, chemical and biological studies of coatings produced by hybrid technologies (HT), which combine primer layer and calcium phosphate (CaP) coating. The first HT type combines the method of vacuum arc titanium primer layer deposition on a stainless steel substrate with the following micro-arc oxidation (MAO) in phosphoric acid solution with addition of calcium compounds to achieve high supersaturated state. MAO CaP coatings feature high porosity (2-8%, pore size 5-7 μm) and surface morphology with the thickness greater than 5 μm. The thickness of Ti primer layer is 5-40 μm. Amorphous MAO CaP coating micro-hardness was measured at maximum normal load Fmax = 300 mN. It was 3.1 ± 0.8 GPa, surface layer elasticity modulus E = 110 ± 20 GPa, roughness Ra = 0.9 ± 0.1 μm, Rz = 7.5 ± 0.2 μm, which is less than the titanium primer layer roughness. Hybrid MAO CaP coating is biocompatible, able to form calcium phosphates from supersaturated body fluid (SBF) solution and also stimulates osteoinduction processes. The second HT type includes the oxide layer formation by thermal oxidation and then CaP target radio frequency magnetron sputtering (RFMS). Oxide-RFMS CaP coating is a thin dense coating with good adhesion to the substrate material, which can be used for metal implants. The RFMS CaP coating has thickness 1.6 ± 0.1 μm and consists of main target elements calcium and phosphorus and Ca/P ratio 2.4. The second HT type can form calcium phosphates from SBF solution. In vivo study shows that hybrid RFMS CaP coating is biocompatible and produces fibrointegration processes.

Язык оригиналаАнглийский
Номер статьи020047
ЖурналAIP Conference Proceedings
Том1760
DOI
СостояниеОпубликовано - 2 авг 2016
СобытиеInternational Conference on Physics of Cancer: Interdisciplinary Problems and Clinical Applications 2016, PC 2016 - Tomsk, Российская Федерация
Продолжительность: 22 мар 201625 мар 2016

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Подробные сведения о темах исследования «Hybrid calcium phosphate coatings for implants». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать