High-Temperature Electrical Conductivity of LaCr1-xCoxO3 Ceramics

Alexander Bonet, Moritz To Baben, Nahum Travitzky, Peter Greil

Результат исследований: Материалы для журналаСтатья

16 Цитирования (Scopus)

Аннотация

LaCr1-xCoxO3 solid-solution ceramics (x = 0.0-0.3) were prepared by pressureless sintering of a submicrometer powder. The powder was synthesized by a modified glycine nitrate process at 800°C. The electrical conductivity of the material sintered at 1600°C was measured by AC four-wire method from room temperature to 1200°C. While undoped (x = 0) LaCrO3 revealed semiconductivity dominated by thermally activated mobility of small polarons over a vast temperature range, substitution of Co for Cr gave rise for a pronounced enhancement of conductivity at temperatures >200°C. XPS analysis showed that the concentration of Cr4+ on the Cr-site and Co2+ at the Co-site increased with Co substitution suggesting a thermally activated redox reaction Cr3+ + Co3+→Cr4+ + Co2+ to create additional charge carriers. Thus, Co doping offers a high potential for designing the electrical conductivity making LaCr1-xCoxO3 an interesting resistivity material for high temperature applications.

Язык оригиналаАнглийский
Страницы (с-по)917-921
Число страниц5
ЖурналJournal of the American Ceramic Society
Том99
Номер выпуска3
DOI
СостояниеОпубликовано - 1 мар 2016
Опубликовано для внешнего пользованияДа

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

Fingerprint Подробные сведения о темах исследования «High-Temperature Electrical Conductivity of LaCr<sub>1-x</sub>Co<sub>x</sub>O<sub>3</sub> Ceramics». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать