High-rate reactive deposition of transparent SiO2 films containing low amount of Zr from molten magnetron target

Jindrich Musil, Vaclav Satava, Pavel Baroch

Результат исследований: Материалы для журналаСтатья

20 Цитирования (Scopus)

Аннотация

The paper reports on a reactive deposition of transparent SiO2 films with a low amount (≤ 3 at.%) of Zr prepared from the molten target using the AC pulsed dual magnetron. It is shown that the deposition rate a D of the transparent oxide film strongly increases at the critical target power density (Wt)cr when the solid target starts to melt and the magnetron operates with a molten target. In this case, the evaporation of target material plays a dominant role in the reactive deposition of thin films. This process is called the ionized magnetron evaporation. Oxide films reactively deposited from the molten target are well transparent and highly elastic. The maximum deposition rate of the transparent oxide film achieved in our experiments is 814 nm/min.

Язык оригиналаАнглийский
Страницы (с-по)775-777
Число страниц3
ЖурналThin Solid Films
Том519
Номер выпуска2
DOI
СостояниеОпубликовано - 1 ноя 2010

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Подробные сведения о темах исследования «High-rate reactive deposition of transparent SiO<sub>2</sub> films containing low amount of Zr from molten magnetron target». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать