Granulated foam glass-ceramic material from zeolitic rocks

Vladimir I. Vereshagin, Svetlana N. Sokolova

Результат исследований: Материалы для журналаСтатья

15 Цитирования (Scopus)

Выдержка

The objective of this research work was to investigate the production of granulated foam glass-ceramic material from zeolitic rocks. The investigations have shown that grinding raw materials to particle size less than 0.5 mm and adding 13.8% of alkali content provide production of material with the following properties: particle density - 340 kg/m3, strength - 1.6 MPa and water adsorption - 13% at firing temperature of 850 °C. Expanded zeolite with alkali content is a material of glass-ceramic composition with amorphous part of 38.6% and crystalline part of 61.4% that gives higher strength in comparison with sponge glass.

Язык оригиналаАнглийский
Страницы (с-по)999-1003
Число страниц5
ЖурналConstruction and Building Materials
Том22
Номер выпуска5
DOI
СостояниеОпубликовано - мая 2008

Отпечаток

Alkalies
Glass ceramics
Ceramic materials
Foams
Rocks
Zeolites
Raw materials
Particle size
Crystalline materials
Adsorption
Glass
Water
Chemical analysis
Temperature

ASJC Scopus subject areas

  • Civil and Structural Engineering
  • Materials Science(all)

Цитировать

Granulated foam glass-ceramic material from zeolitic rocks. / Vereshagin, Vladimir I.; Sokolova, Svetlana N.

В: Construction and Building Materials, Том 22, № 5, 05.2008, стр. 999-1003.

Результат исследований: Материалы для журналаСтатья

@article{16e6a0cf5a4d463ba846f45921971280,
title = "Granulated foam glass-ceramic material from zeolitic rocks",
abstract = "The objective of this research work was to investigate the production of granulated foam glass-ceramic material from zeolitic rocks. The investigations have shown that grinding raw materials to particle size less than 0.5 mm and adding 13.8{\%} of alkali content provide production of material with the following properties: particle density - 340 kg/m3, strength - 1.6 MPa and water adsorption - 13{\%} at firing temperature of 850 °C. Expanded zeolite with alkali content is a material of glass-ceramic composition with amorphous part of 38.6{\%} and crystalline part of 61.4{\%} that gives higher strength in comparison with sponge glass.",
keywords = "Building materials, Lightweight aggregates, Processing, Raw materials",
author = "Vereshagin, {Vladimir I.} and Sokolova, {Svetlana N.}",
year = "2008",
month = "5",
doi = "10.1016/j.conbuildmat.2007.01.016",
language = "English",
volume = "22",
pages = "999--1003",
journal = "Construction and Building Materials",
issn = "0950-0618",
publisher = "Elsevier Limited",
number = "5",

}

TY - JOUR

T1 - Granulated foam glass-ceramic material from zeolitic rocks

AU - Vereshagin, Vladimir I.

AU - Sokolova, Svetlana N.

PY - 2008/5

Y1 - 2008/5

N2 - The objective of this research work was to investigate the production of granulated foam glass-ceramic material from zeolitic rocks. The investigations have shown that grinding raw materials to particle size less than 0.5 mm and adding 13.8% of alkali content provide production of material with the following properties: particle density - 340 kg/m3, strength - 1.6 MPa and water adsorption - 13% at firing temperature of 850 °C. Expanded zeolite with alkali content is a material of glass-ceramic composition with amorphous part of 38.6% and crystalline part of 61.4% that gives higher strength in comparison with sponge glass.

AB - The objective of this research work was to investigate the production of granulated foam glass-ceramic material from zeolitic rocks. The investigations have shown that grinding raw materials to particle size less than 0.5 mm and adding 13.8% of alkali content provide production of material with the following properties: particle density - 340 kg/m3, strength - 1.6 MPa and water adsorption - 13% at firing temperature of 850 °C. Expanded zeolite with alkali content is a material of glass-ceramic composition with amorphous part of 38.6% and crystalline part of 61.4% that gives higher strength in comparison with sponge glass.

KW - Building materials

KW - Lightweight aggregates

KW - Processing

KW - Raw materials

UR - http://www.scopus.com/inward/record.url?scp=40649087877&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=40649087877&partnerID=8YFLogxK

U2 - 10.1016/j.conbuildmat.2007.01.016

DO - 10.1016/j.conbuildmat.2007.01.016

M3 - Article

AN - SCOPUS:40649087877

VL - 22

SP - 999

EP - 1003

JO - Construction and Building Materials

JF - Construction and Building Materials

SN - 0950-0618

IS - 5

ER -