Friction and the development of hard alloy surface microstructures during wear

Результат исследований: Материалы для журналаСтатья

3 Цитирования (Scopus)

Аннотация

Investigations of wear in sliding friction of WC-Hadfield steel hard alloy against cast tool steel have been carried out in a broad range of velocities and pressure values. Structural and phase composition variations have been revealed. Friction-affected zone was found to be 450 μm in depth. Structural γ→ α, γ→ epsi; transformation regions are located within 100 μm of the surface. These transformations contributed to the total solid solution deformation hardening.

Язык оригиналаАнглийский
Страницы (с-по)737-742
Число страниц6
ЖурналJournal of Materials Engineering and Performance
Том6
Номер выпуска6
СостояниеОпубликовано - 1997

ASJC Scopus subject areas

  • Materials Science(all)

Fingerprint Подробные сведения о темах исследования «Friction and the development of hard alloy surface microstructures during wear». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать