Foam-glas crystal materials

Результат исследования: Материалы для книги/типы отчетовМатериалы для конференции

Аннотация

The paper describes the foam-glass crystal material production technology via the intermediate product comprising residual crystalline phase. Different factors impact (macroscopic structure, quantity and size of the crystalline phase) on the foam material strength properties has been searched. It has been stated that the material with a hexagonal shape of pores 1-1.5 mm in size and partitions 40-50 μm thick is characterized by the maximum strength. When nanospheroids are formed in the noncrystalline matrix of the foamed material partition, its strength reaches 4.5 MPa which is close to the values of calculated strength (5 MPa).

Язык оригиналаАнглийский
Заголовок главной публикацииProceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012
DOI
Статус публикацииОпубликовано - 2012
Событие2012 7th International Forum on Strategic Technology, IFOST 2012 - Tomsk, Российская Федерация
Длительность: 18 сен 201221 сен 2012

Другое

Другое2012 7th International Forum on Strategic Technology, IFOST 2012
СтранаРоссийская Федерация
ГородTomsk
Период18.9.1221.9.12

    Fingerprint

ASJC Scopus subject areas

  • Management of Technology and Innovation

Цитировать

Kazmina, O. V., Semukhin, B. S., & Mukhortova, A. V. (2012). Foam-glas crystal materials. В Proceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012 [6357558] https://doi.org/10.1109/IFOST.2012.6357558