Fabrication of the Ni3Al-based alloy formed by spark plasma sintering of VKNA powders

L. I. Shevtsova, Alexander Sergeevich Ivashutenko, N. V. Martyushev, R. I. Kuzmin

Результат исследований: Материалы для журналарецензирование

2 Цитирования (Scopus)

Аннотация

The material based on Ni3Al intermetallic has been obtained from the industrial powder of a VKNA type by the method of spark plasma sintering. Materials sintering was conducted at the temperature of 1100 °C, compacting pressure of 20 MPa, and during soaking time equal to 5 minutes. The heating rate of samples amounted to 50 and 200 °C/min. It has been established that the material obtained by sintering at the rate of 50 °C/min possesses a maximum value of density (5.93 g/cm3) and a maximum level of bending strength (∼ 400 MPa).

Язык оригиналаАнглийский
Номер статьи012113
ЖурналIOP Conference Series: Materials Science and Engineering
Том124
Номер выпуска1
DOI
СостояниеОпубликовано - 2 июн 2016
СобытиеInternational Conference on Mechanical Engineering, Automation and Control Systems 2015, MEACS 2015 - Tomsk, Российская Федерация
Продолжительность: 1 дек 20154 дек 2015

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Fingerprint Подробные сведения о темах исследования «Fabrication of the Ni<sub>3</sub>Al-based alloy formed by spark plasma sintering of VKNA powders». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать