Fabrication of Al2O3–ZrO2 ceramics with high porosity and strength

K. S. Kamyshnaya, T. A. Khabas

Результат исследований: Материалы для журналаСтатьярецензирование

Аннотация

This study describes the synthesis of ceramics, in which a micrometre-sized Al2O3–ZrO2 nanopowder was used as an oxide base for the hardening of the materials. To a suspension of this mixed metal oxide, the pore-forming crystallisation additives camphor and carbamide were added to produce ceramics with thin permeable pores. Camphor crystallised in the oxide suspension in the form of single pentagonal stars and сarbamide crystallised in the form of thin elongated needles. The use of the different crystallisation additives allowed the formation of ceramics after sintering that have both permeable and complex pore morphologies, where anisotropic properties were observed using carbamide as an additive but not when camphor was used. The total porosity of the resulting ceramics was 51.3%, with a compressive strength in the range of 17.3–92.3 MPa.

Язык оригиналаАнглийский
Страницы (с-по)1666-1671
Число страниц6
ЖурналCeramics International
Том47
Номер выпуска2
DOI
СостояниеОпубликовано - 15 янв 2021

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Process Chemistry and Technology
  • Surfaces, Coatings and Films
  • Materials Chemistry

Fingerprint Подробные сведения о темах исследования «Fabrication of Al<sub>2</sub>O<sub>3</sub>–ZrO<sub>2</sub> ceramics with high porosity and strength». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать