Enhancement of the positron intensity by a tungsten single-crystal target at the KEKB injector linac

T. Suwada, M. Satoh, T. Sugimura, T. Kamitani, K. Furukawa, K. Umemori, H. Okuno, T. Haruna, R. Hamatsu, T. Sumiyoshi, K. Yoshida, A. P. Potylitsin, I. S. Tropin, R. Chehab

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

1 Цитирования (Scopus)

Аннотация

A new tungsten single-crystal target has been successfully employed at the positron source of the KEKB injector linac. The crystal thickness was determined to be 10.5 mm based on the previous systematic measurements of the positron-production efficiency. The crystal axis, 〈111〉, was precisely aligned to the direction of the 4-GeV primary electron beam. The positron yield increased by ∼25% compared to that for a conventional tungsten plate with a thickness of 14 mm. On the contrary, the heat load on the crystal target decreased by ∼20%. No degradation of the positron-production efficiency was observed since the crystal target was installed in September 2006, and it has been stably operating at the KEK B-factory.

Язык оригиналаАнглийский
Название основной публикацииProceedings of the IEEE Particle Accelerator Conference
Страницы2778-2780
Число страниц3
DOI
СостояниеОпубликовано - 2007
СобытиеIEEE Particle Accelerator Conference, PAC07 - Albuquerque, NM, Соединенные Штаты Америки
Продолжительность: 25 июн 200729 июн 2007

Другое

ДругоеIEEE Particle Accelerator Conference, PAC07
СтранаСоединенные Штаты Америки
ГородAlbuquerque, NM
Период25.6.0729.6.07

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint Подробные сведения о темах исследования «Enhancement of the positron intensity by a tungsten single-crystal target at the KEKB injector linac». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать