Electrochemical hydrogenation after mechanical activated near equiatomic Ti-Ni powder

E. Abdulmenova, O. Vaulina, S. Kulkov

Результат исследований: Материалы для журнала

3 Цитирования (Scopus)


It has been studied an effect of mechanical activation in a planetary ball milling on the electrochemical hydrogenation of Ti-Ni powder near equiatomic content. It has been shown that average particle sizes measured by scanning electron microscope decreased from 11.1 to 7.8 μm up to 30 s mechanical activation, then increased to 33.2 μm for 300 s activation. Beside, with an increase in the time of mechanical activation was formed state with small the coherently diffracting domain which correspond to quasi-amorphous state of material. It has been shown that after hydrogenation, the particle size distribution did not change. There is an incubation time hydrogenation for mechanical activation, when hydrogenation is not occurring. Mechanical activation for more than 30 s leads to the formation of the Ti 2 NiH x phase based on the Ti 2 Ni and 50 s activation is sufficient to form the Ti 2 NiH 0.5 stoichiometry. For a longer mechanical activation a phase with the stoichiometry Ti 2 NiH 0.85 was formed and to obtain the Ti 2 NiH stoichiometry it is necessary to carry out activation for 4.5 hours.

Язык оригиналаАнглийский
Номер статьи12009
ЖурналIOP Conference Series: Materials Science and Engineering
Номер выпуска1
СостояниеОпубликовано - 24 апр 2019
СобытиеInternational Scientific and Technical Youth Conference on Perspective Materials of Constructional and Medical Purpose 2018, PMCP 2018 - Tomsk, Российская Федерация
Продолжительность: 26 ноя 201830 ноя 2018

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Fingerprint Подробные сведения о темах исследования «Electrochemical hydrogenation after mechanical activated near equiatomic Ti-Ni powder». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать