Effects of transient thermal shock loadings on the structure of zirconia ceramics

Результат исследований: Материалы для журналаСтатья


In this paper the influence of thermal shock loadings on the phase composition and microstructure of ZrO2(Y2O3) and ZrO2(MgO) ceramics was studied. It was found that thermal shock strains were no effect on phase composition of ZrO2(Y2O3) ceramics. Reducing the concentration of high-temperature tetragonal t-ZrO2 and cubic c-ZrO2 modifications and rising the content of low-temperature monoclinic m-ZrO2 crystal system with increasing the number of thermal shock strains were observed. The values of region coherent X-ray scattering of ZrO2(Y2O3) ceramics didn't changed, while the crystallite size of ZrO2(MgO) ceramics decreased. The formation of block structure in all studied ceramics was observed, the sizes of the blocks formed in the ZrO2(Y2O3) and ZrO2(MgO) ceramics were slightly different. The formation of the blocks in ZrO2(Y2O3) ceramics occurred on the grain boundaries, while the crystallites in ZrO2(MgO) ceramics were crushed due to phase transformation.

Язык оригиналаАнглийский
Номер статьи012029
ЖурналIOP Conference Series: Materials Science and Engineering
Номер выпуска1
СостояниеОпубликовано - 8 ноя 2016

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Fingerprint Подробные сведения о темах исследования «Effects of transient thermal shock loadings on the structure of zirconia ceramics». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать