Effect of Tb4O7 content on the optical and mechanical properties of transparent ceramics based on MgAl2O4

Результат исследований: Материалы для журналарецензирование

Аннотация

Transparent magnesium aluminate spinel (MgAl2O4, MAS) ceramics doped with different Tb4O7 concentrations from 0,1 to 5 wt% were fabricated by Spark Plasma Sintering (SPS) technique at temperature 1300 °C and uniaxial pressure 140 MPa. The diffuse transmittance of the undoped and Tb4O7-doped MAS-ceramics samples in visible spectral range reaches 65,32% and 54,7% (at λ = 600 nm) respectively. The microhardness varies from 16,62 ± 0,46 to 17,29 ± 0,34 GPa. The effect of terbium oxide on the optical and mechanical properties of MgAl2O4-based transparent ceramics is discussed.

Язык оригиналаАнглийский
Страницы (с-по)2089-2092
Число страниц4
ЖурналMaterials Today: Proceedings
Том19
DOI
СостояниеОпубликовано - 2019
Событие2019 International Conference on Modern Trends in Manufacturing Technologies and Equipment, ICMTMTE 2019 - Sevastopol, Российская Федерация
Продолжительность: 9 сен 201913 сен 2019

ASJC Scopus subject areas

  • Materials Science(all)

Fingerprint Подробные сведения о темах исследования «Effect of Tb<sub>4</sub>O<sub>7</sub> content on the optical and mechanical properties of transparent ceramics based on MgAl<sub>2</sub>O<sub>4</sub>». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать