Effect of structural states in near-surface layers of commercial titanium on its fatigue life and fatigue fracture mechanisms

V. E. Panin, T. F. Elsukova, Yu F. Popkova, Yu I. Pochivalov, Sunder Ramasubbu

Результат исследования: Материалы для журналаСтатья

13 Цитирования (Scopus)

Аннотация

Changes of structural states in near-surface layers of α-titanium strongly affect its fatigue life and fatigue fracture mechanisms. In α-titanium subjected to alternate bending a sliding mode crack develops, resulting in slight delamination of the material. Hydrogenation of α-titanium surface layers preserves their sliding mode cracking but greatly enhances their delamination. Nanostructuring of α-titanium surface layers increases their nanohardness and elastic modulus and causes opening mode cracking. The fatigue life of the material after surface hydrogenation decreases three times, and after surface nanostructuring, it increases four times.

Язык оригиналаАнглийский
Страницы (с... по...)1-7
ЖурналPhysical Mesomechanics
Том18
Номер выпуска1
DOI
Статус публикацииОпубликовано - 2015

    Fingerprint

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Mechanics of Materials
  • Materials Science(all)

Цитировать