Effect of electron beam irradiation on structural phase transformations of zirconia-based composite reinforced by alumina nanofibers and carbon nanotubes

A. A. Leonov, Yu F. Ivanov, M. P. Kalashnikov, E. V. Abdulmenova, V. D. Paygin, A. D. Teresov

Результат исследований: Материалы для журнала

Аннотация

Evolution of microstructure, elemental and phase composition of dense zirconia-based composite under irradiation with electron beam were investigated. Tetragonal zirconia-based composite reinforced by 5 wt% alumina nanofibers and 0.5 wt% single-walled carbon nanotubes was prepared by spark plasma sintering at a temperature of 1500?C. Irradiation of the composite was carried out with a low-energy pulsed electron beam of submillisecond duration in the following mode: beam energy density 15 J•cm-2; pulse duration 200 μs; pulse repetition rate 0.3 s-1; pulses quantity 10, 20, 30 and 40; residual gas pressure (argon) in the working camera 10-2 Pa. It has been established that electron beam treatment leads to the formation of modified multilayered surface, the thickness of which varies from 6 to 40 μm. Redistribution of Al atoms in the modified surface layer was detected. The phase evolution dependent on the quantity of irradiation pulses and manifested in the crystalline structure of material.

Язык оригиналаАнглийский
Номер статьи012106
ЖурналJournal of Physics: Conference Series
Том1393
Номер выпуска1
DOI
СостояниеОпубликовано - 28 ноя 2019
Событие14th International Conference on Gas Discharge Plasmas and Their Applications, GDP 2019 - Tomsk, Российская Федерация
Продолжительность: 15 сен 201921 сен 2019

    Fingerprint

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Цитировать