Dynamics of hydrogen accumulation and radiation-stimulated release from steels

Результат исследований: Материалы для журналаСтатья

8 Цитирования (Scopus)

Аннотация

Hydrogen accumulation during electrolytic saturation of 12Kh18N10T and 12Kh12M1BFR steels, as well as during thermally and radiation-stimulated hydrogen release from the same materials, was studied. It was shown that there is a critical hydrogen concentration in the sample, which is reached in 50 h for this saturation method (1 M H2SO4 electrolyte, current density is 0.5 A/cm2). Initially, hydrogen is trapped at low-temperature (400-500°C) traps of several types in surface layers. At saturation times of 50 h and longer, hydrogen penetrates to high-temperature (800-900°C) traps in the sample bulk. Under electron irradiation of saturated samples, the hydrogen yield nonlinearly increases with electron current density and energy above 40 keV. It was concluded that electronic processes (Auger process and plasmon excitation) play a dominant role in hydrogen diffusion and desorption activation.

Язык оригиналаАнглийский
Страницы (с-по)236-240
Число страниц5
ЖурналJournal of Surface Investigation
Том4
Номер выпуска2
DOI
СостояниеОпубликовано - 1 апр 2010

ASJC Scopus subject areas

  • Surfaces, Coatings and Films

Fingerprint Подробные сведения о темах исследования «Dynamics of hydrogen accumulation and radiation-stimulated release from steels». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать