Development of ideas about graded nature of material deformation affected by network of thermal fatigue cracks

S. V. Panin, P. O. Maruschak, P. S. Lyubutin, I. V. Konovalenko, B. B. Ovechkin

Результат исследований: Материалы для книги/типы отчетовМатериалы для конференции

Аннотация

Within the concept of physical mesomechanics of materials and fracture mechanics, the peculiarities of deformation and failure of heat resistant steel 25Kh1M1F with a network of thermal fatigue cracks are investigated. The main regularities and characteristic stages of the deformation process in specimens from steel 25Kh1M1F affected volumetrically by a network of cracks under localisation of plastic strain are found and described numerically.

Язык оригиналаАнглийский
Название основной публикации19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012
ИздательEuropean Conference on Fracture, ECF
СостояниеОпубликовано - 2012
Событие19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012 - Kazan, Российская Федерация
Продолжительность: 26 авг 201231 авг 2012

Другое

Другое19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012
СтранаРоссийская Федерация
ГородKazan
Период26.8.1231.8.12

ASJC Scopus subject areas

  • Safety, Risk, Reliability and Quality

Fingerprint Подробные сведения о темах исследования «Development of ideas about graded nature of material deformation affected by network of thermal fatigue cracks». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать