Degradation of structure and properties of rail surface layer at long-term operation

V. E. Gromov, Yury Fedorovich Ivanov, R. S. Qin, O. A. Peregudov, K. V. Aksenova, O. A. Semina

Результат исследований: Материалы для журналаСтатья

3 Цитирования (Scopus)

Аннотация

The microstructure evolution and properties variation of the surface layer of rail steel after passed 500 and 1000 million tons of gross weight (MTGW) have been investigated. The wear rate increases to 3 and 3.4 times after passed 500 and 1000 MTGW, respectively. The corresponding friction coefficient decreases by 1.4 and 1.1 times. The cementite plates were destroyed and formed the cementite particles of around 10–50nm in size after passed 500 MTGW. The early stage dynamical recrystallisation was observed after passed 1000 MTGW. The mechanisms for these have been suggested. The large number of bend extinction contours is revealed in the surface layer. The internal stress field is evaluated.

Язык оригиналаАнглийский
Страницы (с-по)1-6
Число страниц6
ЖурналMaterials Science and Technology (United Kingdom)
Том33
Номер выпуска12
DOI
СостояниеПринято/в печати - 11 фев 2017

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Подробные сведения о темах исследования «Degradation of structure and properties of rail surface layer at long-term operation». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать

    Gromov, V. E., Ivanov, Y. F., Qin, R. S., Peregudov, O. A., Aksenova, K. V., & Semina, O. A. (Принято в печать). Degradation of structure and properties of rail surface layer at long-term operation. Materials Science and Technology (United Kingdom), 33(12), 1-6. https://doi.org/10.1080/02670836.2017.1287983